Characterization of hydrated silicate glass microballoons

Published online by Cambridge University Press:  31 January 2011

Hiroshi Isobe ,
Ichiro Tokunaga ,
Noriyoshi Nagai  and
Katsumi Kaneko
Hiroshi Isobe
Affiliation:
Technical Center, Fuji Chemical Co., Ltd., Nakatsugawa 509–91, Japan
Ichiro Tokunaga
Affiliation:
Department of Chemistry, Faculty of Science, Chiba University, Chiba 263, Japan
Noriyoshi Nagai
Affiliation:
Department of Chemistry, Faculty of Science, Chiba University, Chiba 263, Japan
Katsumi Kaneko
Affiliation:
Department of Chemistry, Faculty of Science, Chiba University, Chiba 263, Japan
Get access

Abstract

Glass microballoons (GB) of about 1 μm in diameter were prepared by ultrasonic spray pyrolysis from sodium silicate solution. A silica-rich type of glass microballoons (SB) was prepared by acid treatment of GB. The structural changes of both microballoons with thermal treatment up to 973 K were examined. Both GB and SB showed properties similar to hydrated sodium silicate glass, to some extent. SB was more thermally stable than GB, but the spherical structures of both microballoons were collapsed by heating at 973 K; cristobalite was observed in samples heated at 973 K. The loosely and tightly incorporated water molecules evolved up to 573 K and near 850 K, respectively. The crystallization of cristobalite caused tightly incorporated water molecules to develop. The ultramicropores accessible only to H2O molecules in SB gradually decreased by heating and disappeared by heating at 773 K.

Type
Articles
Information
Journal of Materials Research , Volume 11 , Issue 11 , November 1996 , pp. 2908 - 2915
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Iler, R. K., The Chemistry of Silica (John Wiley and Sons Inc., New York, 1979), p. 625.Google Scholar
2.Bhambhani, M.R., Cutting, P.A., Sing, K. S. W., and Turk, D.H., J. Colloid Interface Sci. 38, 109 (1972).CrossRefGoogle Scholar
3.Hair, M.L., ACS Symp. Ser. 137, 1 (1982).Google Scholar
4.Kondo, S., Ads. Sci. Technol. 3, 109 (1986).CrossRefGoogle Scholar
5.Gallas, J. P., Lavalley, J. C., Burneau, A., and Barres, O., Langmuir 7, 1235 (1991).CrossRefGoogle Scholar
6.Vail, J. G., Soluble Silicates (Reinhold, New York, 1952).Google Scholar
7.Dent Glasser, L. S. and Lee, C.K., J. Appl. Chem. Biotechnol. 21, 127 (1971).CrossRefGoogle Scholar
8.Sweet, J. R. and White, W.B., Physics Chem. Glasses 10, 246 (1969).Google Scholar
9.Wu, C. K., J. Am. Ceram. Soc. 63, 453 (1980).CrossRefGoogle Scholar
10.Moriya, Y. and Nogami, M., J. Non-Cryst. Solids 38–39, 667 (1980).CrossRefGoogle Scholar
11.Tomazawa, M., Takata, M., Acocella, J., Watson, E.B., and Takamori, T., Yogyo-Kyokai-Shi 91, 377 (1983).CrossRefGoogle Scholar
12.Uchino, T., Sakka, T., and Iwasaki, M., J. Am. Ceram. Soc. 74, 306 (1991).CrossRefGoogle Scholar
13.Farnand, J. R. and Puddington, I.E., Powder Technol. 22, 11 (1979).CrossRefGoogle Scholar
14.Koie, S., Hyomen 18, 52 (1980).Google Scholar
15.Verweij, H., DeWith, G., and Veeneman, D., J. Mater. Sci. 20, 1069 (1985).CrossRefGoogle Scholar
16.Liu, J. G. and Wilcox, D. L. Sr, J. Mater. Res. 10, 84 (1995).CrossRefGoogle Scholar
17.Kaneko, K., Isobe, H., Katori, T., Tokunaga, I., Gouda, T., Suzuki, T., Ozeki, S., and Okuda, K., Colloids Surf. A 74, 47 (1993).CrossRefGoogle Scholar
18.Ishizawa, H., Sakurai, O., Mizutani, N., and Kato, M., Am. Ceram. Soc. Bull. 65, 1399 (1986).Google Scholar
19.Sing, K. S. W., Everett, D. H., Haul, R. A. W., Moscou, L., Pierotti, R. A., Rouquerol, J., and Siemieniewska, T., Pure Appl. Chem. 57, 603 (1985).CrossRefGoogle Scholar
20.Cranston, R. W. and Inkley, F. A., Adv. Catalysis 9, 143 (1957).Google Scholar