Direct correlation of microtwin distribution with growth face morphology of CVD diamond films by a novel TEM technique

Published online by Cambridge University Press:  03 March 2011

Z.L. Wang ,
J. Bentley ,
R.E. Clausing ,
L. Heatherly  and
L.L. Horton
Z.L. Wang*
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6376, and Department of Materials Science and Engineering, The University of Tennessee, Knoxville, Tennessee 37996
J. Bentley
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6376
R.E. Clausing
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6376
L. Heatherly
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6376
L.L. Horton
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6376
*
a)Send all correspondence to this author at current address, Metallurgy Division, NIST, Building 223, Room B106, Gaithersburg, Maryland 20899.
Get access

Abstract

A thick as-grown diamond film was examined directly by conventional transmission electron microscopy (TEM) without thinning, and the important microstructures near the growth surface were characterized. Specimen preparation for TEM involved simply fracturing the film; some of the diamond grains located on the specimen edge were thin enough to be directly examined by TEM. The 3-D topography of the diamond grains located at the intersection of the growth and the fracture surfaces was obtained using secondary electron images, so that the 2-D projected grain geometry could be derived easily to help interpret the TEM images. A diamond film grown with a 〈001〉 texture and having grains 2–3 μm diameter with {001} facets parallel to the substrate and four inclined {111} facets was examined. Grains with fracture surfaces that intersected the top (001) facet, grains with fractures that intersected only {111} facets, and unfractured grains were studied. It was found that the core volume bounded by the (001) top facet and its projected column defined by orthogonal internal {110} were free from microtwins, but contained a few dislocations. The remaining volume around this core, bounded by {111} facets (or grain boundaries) and the internal {110}, was filled with microtwins. The microtwins were not merely at the {111} surfaces. Our results reveal a growth mechanism in which microtwins are formed as material is added to {111} but not {001}. The formation of microtwins in CVD diamond is thus clearly associated with growth on {111} surface facets.

Type
Articles
Information
Journal of Materials Research , Volume 9 , Issue 6 , June 1994 , pp. 1552 - 1561
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Ma, G-H.M., Lee, Y. H., and Glass, J. T., J. Mater. Res. 5, 2367 (1990).CrossRefGoogle Scholar
2Clausing, R. E., Heatherly, L., and More, K. L., Surf. Coating Technol. 39/40, 199 (1990).CrossRefGoogle Scholar
3Williams, B. E. and Glass, J. T., J. Mater. Res. 4, 373 (1989).CrossRefGoogle Scholar
4Narayan, J., J. Mater. Res. 5, 2414 (1990).CrossRefGoogle Scholar
5Wang, Z. L., Bentley, J., Clausing, R. E., Heatherly, L., and Horton, L. L., in Applications of Diamond Films and Related Materials, edited by Tzeng, Y., Yoshikawa, M., Murakawa, M., and Feldman, A. (Elsevier, Amsterdam, 1991), p. 489.Google Scholar
6Angus, J. C. and Hayman, C., Science 241, 913 (1988).CrossRefGoogle Scholar
7Clausing, R. E., Heatherly, L., Specht, E. D., and More, K. L., in New Diamond Science and Technology, edited by Messier, R., Glass, J. T., Butler, J. E., and Roy, R. (Mater. Res. Soc. Symp. Int. Proc. NDST–2, Pittsburgh, PA, 1991), p. 575.Google Scholar
8Wang, Z. L., Clausing, R. E., Heatherly, L., and Horton, L. L., unpublished.Google Scholar
9Zhu, W., Badzian, A. R., and Messier, R., J. Mater. Res. 4, 659 (1989).CrossRefGoogle Scholar
10Kaae, J. L., Gantzel, P. K., Chin, J., and West, W. P., J. Mater. Res. 5, 1480 (1990).CrossRefGoogle Scholar
11Hetherington, A. V., Wort, C. J. H., and Southworth, P., J. Mater. Res. 5, 1591 (1990).CrossRefGoogle Scholar
12Badzian, A. R., Badzian, T., Wang, X. H., and Hartnett, T., in New Diamond Science and Technology, edited by Messier, R., Glass, J. T., Butler, J. E., and Roy, R. (Mater. Res. Soc. Symp. Int. Proc. NDST–2, Pittsburgh, PA, 1991) p. 549.Google Scholar
13Stuart, S., Prawer, S., Hoffman, A., and Moodie, A., in Evolution of Thin Film and Surface Microstructure, edited by Thompson, C. V., Tsao, J. Y., and Srolovitz, D. J. (Mater. Res. Soc. Symp. Proc. 202, Pittsburgh, PA, 1991), p. 217.Google Scholar
14Meakin, D., Stoemenos, J., Migliorato, P., and Economou, N. A., J. Appl. Phys. 61, 5031 (1987).CrossRefGoogle Scholar
15Van der Drift, A., Philips Res. Rep. 22, 267 (1967).Google Scholar
16Wild, Ch., Herres, N., and Koidl, P., J. Appl. Phys. 68, 973 (1990).CrossRefGoogle Scholar
17Wang, Z. L., Horton, L. L., Clausing, R. E., Heatherly, L., and Bentley, J., Proc. 50th Annual Meeting of Electron Microscopy Soc. America (Boston), edited by Bailey, G. W., Bentley, J., and Small, J. A. (San Francisco Press, San Francisco, CA, 1992), p. 336.Google Scholar
18Wang, Z. L., Bentley, J., Clausing, R. E., Heatherly, L., and Horton, L. L., Proc. 51st Annual Meeting of Microscopy Society of America (Boston), edited by Bailey, G. W. and Rieder, E. L. (San Francisco Press, San Francisco, CA, 1993), p. 1006.Google Scholar