Infiltration of C/SiC composites with silica sol-gel solutions: Part II. Infiltration under isostatic pressure and oxidation resistance

Published online by Cambridge University Press:  31 January 2011

Mario Aparicio  and
Alicia Durán
Mario Aparicio
Affiliation:
Instituto de Cerámica y Vidrio (CSIC), E-28500 Arganda del Rey, Madrid, Spain
Alicia Durán
Affiliation:
Instituto de Cerámica y Vidrio (CSIC), E-28500 Arganda del Rey, Madrid, Spain
Get access

Abstract

An infiltration process that uses silica sol-gel solutions was developed to protect C/SiC composites against oxidation. The infiltration is assisted using isostatic pressure. Different process parameters including substrate porosity and solution concentration and viscosity were varied to optimize the infiltration effectiveness. Applied pressure enhances penetration of solutions, reducing the importance of viscosity, an important process variable for dipping infiltration. The effectiveness of the isostatic pressure infiltration method, evaluated through the total weight gains and pore-size distribution of infiltrated samples, is compared with results of dipping infiltration. The oxidation behavior of the infiltrated samples, was evaluated by stepwise oxidation test as well as isothermal tests at 1200 and 1600 °C. The infiltrated SiO2 protects the C/SiC substrate, reducing the burnoff rate of C fibers at low temperature and delaying the oxidation of SiC.

Type
Articles
Information
Journal of Materials Research , Volume 14 , Issue 11 , November 1999 , pp. 4239 - 4245
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Vogel, W.D. and Spelz, U., Ceram. Trans. 51, 255 (1995).Google Scholar
2.Haug, T., Ostertag, R., Knabe, H., Ehrman, U., and Woltersdorf, J., in Proc. 6th European Conf. on Composite Materials, Bordeaux, Sept. 20–24, 1993, p.767.Google Scholar
3.Aparicio, M. and Durán, A., J. Mater. Res. 14, 4230 (1999).CrossRefGoogle Scholar
4.Delannay, F., Froyen, L., and Deruyttere, A., J. Mater. Sci. 22, 1 (1987).CrossRefGoogle Scholar
5.Defay, R., Prigogine, I., Bellemans, A., and Everett, D.H., Surface Tension and Adsorption (Longmans, Green & Co., London, United Kingdom, 1966), p. 1.Google Scholar
6.Alonso, A., Pamies, A., Narciso, J., Garcia-Cordovilla, C., and Louis, E., Metallurgical Transactions A 24A, 1423 (1993).CrossRefGoogle Scholar
7.Semlak, K.A. and Rhines, F.N., Trans. Metall. Soc. AIME 212, 325 (1958).Google Scholar