Twinning Mlcrostructure and Charge Ordering in the Colossal Magnetoresistive Manganite Nd1/2Sr1/2MnO3

Published online by Cambridge University Press:  02 July 2020

Z. P. Luo
Affiliation:
Materials Science Division, Argonne National Laboratory, Argonne, Illinois60439, USA
D. J. Miller
Affiliation:
Materials Science Division, Argonne National Laboratory, Argonne, Illinois60439, USA
J. F. Mitchell
Affiliation:
Materials Science Division, Argonne National Laboratory, Argonne, Illinois60439, USA
Get access

Extract

Charge ordering (C.O.) in the colossal magnetoresistive (CMR) manganites gives rise to an insulating, high-resistance state. This charge ordered state can be melted into a low-resistance metallic-like state by the application of magnetic field. Thus, the potential to attain high values of magnetoresistance with the application of small magnetic fields may be aided by a better understanding of the charge-ordering phenomenon. This study focused on microstructural characterization in Nd1/2Sr1/2MnO3. In Nd1/2Sr1/2MnO3, the nominal valence of Mn is 3.5+. On cooling, charge can localize and lead to a charge ordering between Mn 3+ and Mn 4+. The ordering of charge results in a superlattice structure and a reduction in symmetry.

Thin foil specimens were prepared from bulk samples by conventional thinning and ion milling (at LN2 temperature) methods. The TEM work was carried out in a Philips CM30 at 300 kV with a Gatan LN2 cold stage, and a JEM 4000EX with a resolution of 0.17 nm at 400 kV for HREM observation.

Type
Ceramics & Minerals
Copyright
Copyright © Microscopy Society of America

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

References:

1.)Mitchell, J.F. et al., Phys. Rev. B 54 (1996) 6172.CrossRefGoogle Scholar
2.)Radaelli, P.G., Cox, D.E., Marezio, M., and Cheong, S-W., Phys. Rev. B 55 (1997) 3015.CrossRefGoogle Scholar
3.)Woodward, P.M., Cox, D.E., Vogt, T., Rao, C.N.R., and Cheetham, A.K., Chem. Mater. 11 (1999) 3528.CrossRefGoogle Scholar
4.) Supported by the U.S. Department of Energy, Division of Basic Energy Sciences-Material Sciences, under contract W-31-109-Eng-38.Google Scholar