The crystal-structures of the sulphides of mercury

Published online by Cambridge University Press:  14 March 2018

H. E. Buckley  and
W. S. Vernon
W. S. Vernon
Affiliation:
University of Manchester
Get access Rights & Permissions [Opens in a new window]

Extract

Mercuric sulphide, HgS, occurs in nature as two well-known modifications, cinnabar and metacinnabarite. The latter is some what rare and occurs as black cubic crystals possessing the symmetry of the zinc-bleude, i.e. the ditesseral polar-class. It is considered to be identical with chemically precipitated black mercuric sulphide, the density of both being 7.81. Cinnabar is of more common occurrence and is found as well-defined crystals and in the massive state. The crystals are assigned to the trigonal holoaxial class. The rhombohedral angle is 92°30' r correspouding to an axial ratio c/a of 1.1453. The crystals possess a very good cleavage parallel to the prism (21̄1̄)=(101̄0). The rotation of the plane of polarization, for red light traversing the crystal in a direction parallel to the optic axis, is 315° per millimetre, a value roughly eighteen times that of a similar thickness of quartz.

Type
Research Article
Information
Mineralogical magazine and journal of the Mineralogical Society , Volume 20 , Issue 110 , September 1925 , pp. 382 - 392
Copyright
Copyright © The Mineralogical Society of Great Britain and Ireland 1925

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Page 382 note 1 Data from the compilation of Groth, P., Chem. Kryst., 1906, vol. 1, p. 151 Google Scholar.

Page 383 note 1 Mauguin, C., Compt. Rend. Acad. Set. Paris, 1923, vol. 176, pp. 1483 Google Scholar. [Min. Abstr., vol. 2, p. 330.]

Page 383 note 2 Kolkmeijer, N. H., Bijvoet, J. M., and Karssen, A., Proc. Sect. Sci. K. Akad. Wetenseh. Amsterdam, 1924, vol. 27, pp. 390, 847Google Scholar; Reeueil Tray. Chim. Pays-Bas, 1924, vol. 43, pp. 677, 894. [Min. Abstr., vol. 2, p. 511.]

Page 384 note 1 Bradley, A. J., The crystal structure of metallic arsenic. Phil. Mag., 1924, ser. 6, vol. 47, pp. 657–671 CrossRefGoogle Scholar. [Min. Abstr, vol. 2, p. 331.]

Page 391 note 1 Larmor, J., Proc. Roy. Soc. London, 1921, ser. A, vol. 99, pp. 1–10.CrossRefGoogle Scholar

Page 392 note 1 Mauguin, C., Compt. Rend. Acad. Sci. Paris, 1924, vol. 178, p. 1913 Google Scholar. [Min. Abstr, vol. 2, p. 510.]