Characterization of local hydride re-orientation in high burn-up PWR fuel rods induced by high pressure at high temperatures

Published online by Cambridge University Press:  23 December 2016

Y. Yan ,
T. Smith ,
Z. Burns  and
B Bevard
Y. Yan*
Affiliation:
Oak Ridge National laboratory, Oak Ridge, TN-37831
T. Smith
Affiliation:
Oak Ridge National laboratory, Oak Ridge, TN-37831
Z. Burns
Affiliation:
Oak Ridge National laboratory, Oak Ridge, TN-37831
B Bevard
Affiliation:
Oak Ridge National laboratory, Oak Ridge, TN-37831
*
*(Email: yy9@ornl.gov)
Get access

Abstract

Hydride re-orientation in high burn-up PWR fuel rods was induced by high pressure at high temperatures. The high-burnup specimens were sectioned from PWR rods taken from a 15×15 assembly of the H.B. Robinson (HBR) Unit 2 reactor. Out-of cell benchmark tests performed on unirradiated hydrided Zircaloy-4 specimens were conducted to determine the appropriate temperature, pressure, cooling rate, and number of cooling cycles for the reorientation of the irradiated in-cell specimens. The in-cell hydride reorientation tests were performed using highburnup fuel specimens under a hoop stress ≈145 MPa at 400ºC. The specimens were heated to the target temperature of 400ºC, held for 3 hours, cooled at 1ºC/min to 170ºC,and then heated at 1ºC/min to the target temperature again for five cycles. Post test metallographic examinations showed that a significant amount of radial hydrides were induced in the HBR fuel rods. The length of radial hydride was up to 60 µm. For unirradiated materials, the ductility of the radial hydride treated specimens is significantly reduced as compared to the as-hydrided specimens having the same hydrogen concentration (≈300 wppm in this work). The mechanical testing on irradiated fueled samples with hydride reorientation experiments have been performed, and will be reported separately in the near future.

Keywords

Zrradiation effectsnuclear materials
Type
Articles
Information
MRS Advances , Volume 2 , Issue 11: Scientific Basis for Nuclear Waste Management XL , 2017 , pp. 591 - 596
Copyright
Copyright © Materials Research Society 2016 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

This manuscript has been authored by UT-Battelle, LLC under Contract No. DE-AC05-00OR22725 with the U.S. Department of Energy. The United States Government retains and the publisher, by accepting the article for publication, acknowledges that the United States Government retains a nonexclusive, paid-up, irrevocable, world-wide license to publish or reproduce the published form of this manuscript, or allow others to do so, for United States Government purposes. The Department of Energy will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan (http://energy.gov/downloads/doe-public-access-plan).

References

REFERENCES

Billone, M. C., Yan, Y., Burtseva, T., and Daum, R., “Cladding Embrittlement during Postulated Loss-of-Coolant Accidents,” NUREG/CR–6967 ANL-07/04 (2008).Google Scholar
Yan, Y., Burtseva, T. A., and Billone, M. C., “Post-quench Ductility Results for North Anna High burnup 17×17 ZIRLO Cladding with Intermediate Hydrogen Content,” ANL letter report to NRC, April 17, 2009.Google Scholar
Billone, M. C., Burtseva, T., and Yan, Y.. “Overview of Spent Nuclear Fuel Program: Test Plan and High Burnup Cladding at ANL,” NRC Program Review Meeting, Argonne National Laboratory, Argonne, IL, July 7, 2010.Google Scholar
Daum, R., Tsai, H., Liu, Y., and Billone, M., “High-Burnup Cladding Mechanical Performance during Cask Storage and Post-Storage Handling and Transportation,” Nuclear Safety Research Conference, Washington, D.C., October 25-27, 2004.Google Scholar
Billone, M. C., Burtseva, T., and Einzuger, R.E., “Dutile-to-Brittle Transition Temperature for High-Burnup Cladding Alloys Exposed to Simulated Drying-Storage Condition,” J. Nucl. Mater. 433, 431 (2013).Google Scholar
Cuta, J., “Temperature Histories in Typical Dry Storage Conditions,” Review Meeting of Argonne’s High-Burnup SNF Transport Program, Argonne, IL, July 7, 2010.Google Scholar
Yan, Y., Blackwell, A. S., Plummer, L. K., Radhakrishnan, B., Gorti, S. B., and Clarno, K. T., “Observation and Mechanism of Hydride in Zircaloy-4 and Local Radial Hydride Induced by High Pressure at High Temperatures,” 2013 International High-Level Radioactive Waste Management, Albuquerque, NM, April 28 – May 2, 2013.Google Scholar
Ruzauska, E.J. and Fardell, K. N., “Design, Operation, and Performance Data for High Burnup PWR Fuel from the H.B. Robinson Plant for Use in the NRC Experimental Program at Argonne National Laboratory,” EPRI report 1001558, May 2001.Google Scholar
Une, K., Nogita, K., Kashibe, S., Toyonaga, T., and Amaya, M., “Effect of Irradiation-Induced Microstructural Evolution on High Burnup Fuel Behavior,” Proceedings of the 1997 International Topical Meeting on LWR Fuel Performance, Portland, OR, March 2-6, 1997, pp. 478–489.Google Scholar