An Assessment of ECR Argon Plasma Etching Damage on Si and SiO2 Interfaces

Published online by Cambridge University Press:  25 February 2011

C. W. Nam ,
S. Ashok ,
W. Tsai  and
M. E. Day
C. W. Nam
Affiliation:
Center for Electronic Materials and Processing, The Pennsylvania State University, University Park, PA 16802
S. Ashok
Affiliation:
Center for Electronic Materials and Processing, The Pennsylvania State University, University Park, PA 16802
W. Tsai
Affiliation:
Varian Research Center, Palo Alto, CA 94304–1025
M. E. Day
Affiliation:
Varian Research Center, Palo Alto, CA 94304–1025
Get access

Abstract

Electron cyclotron resonance (ECR) argon plasma has been used (to etch the native oxide on Si and thermal SiO2. The Schottky barrier height modification on both n- and p-Si has been studied as a function of substrate bias and etch time. Deep Level Transient Spectroscopy (DLTS) measurements show clear peaks on both p- and n-Si, but wish low levels of trap concentrations (1012-1013cm−3), and decreasing with depth from the surface. The effects of thermal oxide etching on the Si/SiO2 interface have been estimated with MOS capacitors. Negative flat-voltage shift is observed after argon plasma exposure, which removes the thermal oxide at a rate of over 100 Å/min at 50 V bias. C-V measurements show an order of magnitude increase in interface trap density.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 279: Symposium A – Beam-Solid Interactions–Fundamentals and Applications , 1992 , 861
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Salimian, S., Cooper, C. B. III, and Ellingboe, A., Appl. Phys. Lett. 56, 1311 (1990).Google Scholar
2. Felch, S. B., Salimian, S., and Hodul, D. T., J. Vac. Sci. Technol. B 10, 1320 (1992)Google Scholar
3. Salimian, S. and Delfino, M., J. Appl. Phys. 70, 3970, (1991)Google Scholar
4. Fonasti, S. J., Ashok, S., and Singh, R., Appl. Phys. Lett. 39, 423, (1981)CrossRefGoogle Scholar
5. Ashok, S., Chow, T.P., and Baliga, B.J., Appl. Phys. Lett. 42, 687, (1983)Google Scholar
6. Pang, S. W., Rathman, D. D., Silversmith, D. J., Mountain, R. W., and DeGraff, P. D., J. Appl. Phys. 54, 3272 (1983)Google Scholar