The Improvement of Dental Composite Properties with Electromagnetically Aligned Nanofiber

Published online by Cambridge University Press:  21 July 2014

Tansel Uyar  and
Dilek Cokeliler
Tansel Uyar
Affiliation:
Department of Biomedical Engineering, Baskent University Baglica Campus, 06530, Ankara, Turkey
Dilek Cokeliler
Affiliation:
Department of Biomedical Engineering, Baskent University Baglica Campus, 06530, Ankara, Turkey Department of Biological System Engineering, University of Wisconsin Madison, Madison, Wisconsin, USA
Get access

Abstract

Because of the aesthetics, handy and low cost features, acrylic resin is the main material in denture fabrication last 40 years. The purpose of this study is to improve mechanical properties of acrylic based dental composites used in dentistry by applying nanofiber approaches. Polymethylmethacrylate (PMMA) is commonly used as a base acrylic denture material with benefits of rapid and easy handling but sometime this material can be fractured or cracked in clinical use because of the strength issues that is frequently used in restorative dentistry in recent years. A wide variety of fillers that are used to produce PMMA composites draw the attention in literature. Using PMMA composite resins with electrospun polyvinylalcohol (PVA) nanofiber fillers is our first novelty. Also the producing and using aligned electrospun fibers as a filler is our second novelty of this practice. PVA was selected as composite filler because of biocompatibility and preparing easily also has non-toxic solvent. Electrospinning system is manufactured that allows manipulation of electric field used in the application of alignment in lab scale. Various auxillary electrode systems are used for different patterns of alignment with the manufactured device and electrode systems produce fibers in different range of diameter. Scanning electron microscopy (SEM) is used for physical characterization and determined the range of fiber diameters. After the optimization of concentration step non-woven and aligned fibers are also analyzed. Non-woven fiber has no unique pattern because of the nature of electrospinning but aligned fibers has crossed lines. These produced fibers structured as layer-by-layer form with different features are used in producing PMMA dental composites with different volume ratios. In the last part of the research, PMMA dental composites are produced with aligned and formless fibers that are characterized with three-point bending test. The maximum flexural strength figure shows that fiber load by weight %0.25 and above improves the maximum. The change of flexural strength, elastic modulus values and toughness are obtained and compared with formless and aligned PVA nanofiber included composite specimens. As a result, mechanical properties of PMMA dental composites are improved with using PVA nanofibers as a filler also with the usage of aligned fibers instead of the formless ones the effects of improvement gets better with maximum values as 5.1 MPa (flexural strength), 0.8 GPa (elastic modulus), 170kJ/m3 (toughness).

Keywords

biomaterialpolymerbiomedical
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1685: Symposium U – Soft Nanomaterials , 2014 , mrss14-1685-u06-12
Copyright
Copyright © Materials Research Society 2014 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Anusavice, K.J. and Phillips, R.W., “Phillips' science of dental materials.”, St. Louis: Elsevier, 89:254–262, 2003.Google Scholar
Altun, C., GATA Medical Journal, 47, 77–82 (2005).Google Scholar
Boaro, L.C.C.B., Gonçalves, F., Guimaraes, T.C., Ferracane, J.L., Versluis, A., Braga, R.R., Dental Materials, 26, 1144–1150 (2010).CrossRefGoogle Scholar
Arakawa, K., Polymer Testing, 29, 1052–1056 (2010).CrossRefGoogle Scholar
Darbar, U.R., Huggett, R. and Harrison, A., Br Dent J, 176, 342–345 (1994).CrossRefGoogle Scholar
Li, R.Z., Ye, L. and Mai, Y., Composites Part, 28, 73–86 (1997).CrossRefGoogle Scholar
Vallittu, P.K., Vojtkova, H. and Lassila, V.P., Acta Odontol. Scand, 53, 392–396 (1995).CrossRefGoogle Scholar
Doshi, J., Reneker, D.H., Journal of Electrostatics, 35, 151–160 (1995).CrossRefGoogle Scholar
Kim, G.H., Journal of Polymer Science: Part B: Polymer Physics, 44, 1426–1433 (2006).CrossRefGoogle Scholar
Rutledge, G.C. and Fridrikh, S.V., Advance Drug Delivery Reviews, 59, 1384–1391 (2007).CrossRefGoogle Scholar
Berdy, D., Chong, H., Paruchuri, S., Yu, J., Hollar, K. and Weitz, D., “Bifurcations in Electrospinning: Splitting a Polymer”, Je Weitz Group, Harvard University, 2005.Google Scholar
Teo, W.E. and Ramakrishna, S., “A review on electrospinning design and nanofibre assemblies”, Institute of Physics Publishing, 89–106, 2006.Google ScholarPubMed
Karatay, O., Dogan, M., Uyar, T., Cokeliler, D. and Kocum, I. C., IEEE Transactions on Nanotechnology, DOI 10.1109/TNANO.2013.2293704, (2013).Google Scholar