Grain Boundary Modification During Neutron Irradiation at Intermediate Temperatures

Published online by Cambridge University Press:  21 March 2011

S. M. Bruemmer ,
D. J. Edwards ,
V. Y. Gertsman  and
E. P. Simonen
S. M. Bruemmer
Affiliation:
Pacific Northwest National Laboratory P.O. Box 999, Richland, WA 99532
D. J. Edwards
Affiliation:
Pacific Northwest National Laboratory P.O. Box 999, Richland, WA 99532
V. Y. Gertsman
Affiliation:
Pacific Northwest National Laboratory P.O. Box 999, Richland, WA 99532
E. P. Simonen
Affiliation:
Pacific Northwest National Laboratory P.O. Box 999, Richland, WA 99532
Get access

Abstract

Grain boundary compositions and near-boundary microstructures have been measured in complex Fe-Cr-Ni alloys after neutron irradiation at intermediate temperatures where nanometer-scale damage promotes structural integrity problems in nuclear reactor systems. Radiation-induced segregation (RIS) and dislocation loop microstructures have been determined as a function of irradiation dose up to 13 dpa and at temperatures near 280°C. The most significant effect on RIS was the grain boundary structure (low-energy special boundaries versus high-energy random boundaries) and composition (enrichment of Cr and Mo) before irradiation. Grain boundary character distribution did not change with irradiation and only high-energy boundaries exhibited significant radiation-induced changes. The initial grain boundary composition in mill-annealed stainless steels was difficult to remove during subsequent irradiation and retarded the development of Cr- and Mo-depleted regions.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 650: Symposium R – Microstructural Processes in Irradiated Materials-2000 , 2000 , R2.1
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Bruemmer, S. M., Simonen, E. P., Scott, P. M., Andresen, P. L., Was, G. S. and Nelson, J. L., J. Nucl Mater., 274, (1999) 294.Google Scholar
2. Scott, P. M., J. Nucl Mater., 211, (1994) 101.Google Scholar
3. Was, G. S. and Bruemmer, S. M., J. Nucl Mater., 216, (1994) 326.Google Scholar
4. Was, G. S. and Andresen, P. L., J. Metals., 44–4, (1992) 8.Google Scholar
5. Nelson, J. L. and Andresen, P. L., Proc. 5th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, ed. Simonen, E. and Gold, R., ANS, 1992, p. 10.Google Scholar
6. Andresen, P. L., Ford, F. P., Murphy, S. M. and Perks, J. M., Proc. 4th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, ed. Cubicciotti, D. and Theus, G., NACE, 1992, p. 1.Google Scholar
7. Gertsman, V. Y. and Bruemmer, S. M., “Study of Grain Boundary Character Along Intergranular Stress Corrosion Crack Paths in Austentic Alloys,” Acta Mater., 2000, in press.Google Scholar
8. Crawford, D. C. and Was, G. S., Metall. Trans., 23A (1992) 1195.Google Scholar
9. Gertsman, V. Y., Tangri, K. and Valiev, R., Acta Mater., 42 (1994) 1785.Google Scholar
10. Pan, Y., Adams, B. L., Olson, T. and Panayotou, N., Acta Mater., 12 (1996) 4685.Google Scholar
11. Bruemmer, S. M. and Thomas, L. E., “High-Resolution Analytical Electron Microscopy Characterization of Corrosion and Cracking at Buried Interfaces,” J. Surface and Interface Analysis, 2000, in press.Google Scholar
12. Doig, P. and Flewitt, P., Metall. Trans., 18A (1987) 399.Google Scholar
13. Karlsson, L., Acta Metall., 36 (1988) 1.Google Scholar
14. Walmsley, J., Spellward, P., Fisher, S. and Jenssen, A., Proc. 7th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, ed. McIlree, A. R. and Bruemmer, S. M., NACE, 1995, p. 985.Google Scholar
15. Simonen, E. P. and Bruemmer, S. M., ibid 14, p. 751.Google Scholar
16. Edwards, D. J., Simonen, E. P. and Bruemmer, S. M., “Nature of the Fine-Scale Defects and Radiation Hardening in Stainless Steels Neutron-Irradiated at 550°K,” this proceeding.Google Scholar
17. Simonen, E. P., Edwards, D. J. and Bruemmer, S. M., Proc. 9th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, ed. Ford, F. P. and Bruemmer, S. M., TMS, 2000, p. 1107.Google Scholar
18. Jenssen, A., Ljungberg, L., Pettersson, K. and Walmsley, J., ibid 14, p. 785.Google Scholar
19. Bruemmer, S. M., Mat. Sci. Forum, 46 (1989) 309.Google Scholar
20. Andresen, P. L., Angeliu, T. M., Catlin, W. R., Young, L. M. and Horn, R. M., “Effect of Deformation on SCC of Unsensitized Stainless Steel,” Corrosion/2000, NACE, 2000, Paper 202.Google Scholar