Laser Ablation Deposition of Diamond-Like Carbon Films

Published online by Cambridge University Press:  01 January 1992

S. Leppävuori ,
J. Levoska ,
J. Vaara  and
O. Kusmartseva
S. Leppävuori
Affiliation:
University of Oulu, Microelectronics and Material Physics Laboratories, SF-90570 Oulu, Finland
J. Levoska
Affiliation:
University of Oulu, Microelectronics and Material Physics Laboratories, SF-90570 Oulu, Finland
J. Vaara
Affiliation:
University of Oulu, Microelectronics and Material Physics Laboratories, SF-90570 Oulu, Finland
O. Kusmartseva
Affiliation:
University of Oulu, Microelectronics and Material Physics Laboratories, SF-90570 Oulu, Finland
Get access

Abstract

Diamond-like carbon (DLC) thin films were prepared by laser ablation deposition. The deposition process was carried out in a vacuum chamber at a base pressure of about 10−5 mbar using the focused beam from either an Nd:YAG laser or an XeCl excimer laser and a pyrolytic graphite target. The peak power density of the laser beam was about 108 W/cm2, and 1010 W/cm2. respectively. The effect of varying power density of the laser beam also was examined. The films were deposited on fused silica and silicon single crystal substrates between room temperature and 600 °C with and without hydrogen addition. The properties of the films were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), micro-Raman and Fourier transform infrared (FTIR) spectrometry, electrical conductivity and optical measurements. The best films were insulating (σ<10−6 Ω−1 cm−1), hard, partly transparent (optical gap 1.3 − 2.2 eV) and smooth without any particulates on the surface.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 285: Symposium I – Laser Ablation in Materials Processing–Fundamentals and Applications , 1992 , 557
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Angus, J. and Hayman, C., Science 241, 913 (1988).Google Scholar
2. Knight, D. and White, W., J. Mater. Res. 4, 385 (1989).Google Scholar
3. Sato, T., Furano, S., Iguchi, S. and Hanabusa, M., Jpn. J. Appl. Phys. 26, L1487 (1987).Google Scholar
4. Davanloo, F., Juengerman, E.M., Jander, D.R., Lee, T.J. and Collins, C.B., J. Mater. Res. 5, 2398 (1990).Google Scholar
5. Pappas, D., Saenger, K., Bruley, J., Krakow, W., Cuomo, J., Gu, T. and Collins, R., J. Appl. Phys. 71, 5675 (1992).Google Scholar
6. Lespade, P., Al-Jishi, R. and Dresselhaus, M., Carbon 20, 427 (1982).Google Scholar
7. Yoshikawa, M., Katagiri, G., Ishida, H. and Ishitani, A., Solid State Commun. 66, 1177 (1988).Google Scholar