Low-temperature Phosphorus Doping To Silicon Using Phosphorus-related Radicals

Published online by Cambridge University Press:  20 March 2012

Taro Hayakawa
Affiliation:
Jpn. Adv. Inst. Sci. & Tech. (JAIST), 1-1 Asahidai, Nomi city, Ishikawa 923-1292 Japan. JST-CREST, 4-1-8 Honcho, Kawaguchi, Saitama 332-0012, Japan.
Yuuki Nakashima
Affiliation:
Jpn. Adv. Inst. Sci. & Tech. (JAIST), 1-1 Asahidai, Nomi city, Ishikawa 923-1292 Japan. JST-CREST, 4-1-8 Honcho, Kawaguchi, Saitama 332-0012, Japan.
Koichi Koyama
Affiliation:
Jpn. Adv. Inst. Sci. & Tech. (JAIST), 1-1 Asahidai, Nomi city, Ishikawa 923-1292 Japan. JST-CREST, 4-1-8 Honcho, Kawaguchi, Saitama 332-0012, Japan.
Keisuke Ohdaira
Affiliation:
Jpn. Adv. Inst. Sci. & Tech. (JAIST), 1-1 Asahidai, Nomi city, Ishikawa 923-1292 Japan.
Hideki Matsumura
Affiliation:
Jpn. Adv. Inst. Sci. & Tech. (JAIST), 1-1 Asahidai, Nomi city, Ishikawa 923-1292 Japan. JST-CREST, 4-1-8 Honcho, Kawaguchi, Saitama 332-0012, Japan.
Get access

Abstract

Phosphorus (P) doped ultra thin n+-layer is formed on crystalline silicon (c-Si) at low substrate temperatures of 80 – 350 °C using radicals generated by the catalytic reaction of phosphine (PH3) with a tungsten catalyzer heated at 1300 °C. The sheet carrier concentration obtained by Hall effect is in the range between 3×1012cm-2 and 8×1012cm-2. The distribution of P atoms obtained by secondary ion mass spectrometry (SIMS) indicates that P atoms locate within the depth of 4 nm from surface and the profile has almost the same distribution independent of any doping conditions such as substrate temperature or radical exposure time. The sheet carrier concentration is 1.15 – 2.12% of the amount of P atoms incorporated through the radical doping. The ratio of activated donors increases with substrate temperature during the radical doping, suggesting that P-related species bonded on the c-Si surface require thermal energy for their activation. Using the n+-layer formed by radical doping, the reduction of surface recombination velocity for n-type c-Si wafer is attempted. The effective minority carrier lifetime of the n-type c-Si sample covered with 6-nm-thick intrinsic amorphous Si (i-a-Si) layers on both side increases from 32 μs to1576 μs by the radical doping of P atoms to n-type c-Si surface, suggesting that the radical doping can be utilized for the formation of passivation layers on a-Si/ n-c-Si hetero-interface.

Keywords

Type
Research Article
Copyright
Copyright © Materials Research Society 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Wakisaka, K., Taguchi, M., Sawada, T., Tanaka, M., Matsuyama, T., Matsuoka, T., Tsuda, S., Nakano, S., Kishi, Y., and Kuwano, Y., Proc. Photovoltaic Specialists Conference; (1991) p.887 Google Scholar
2. Matsumura, H., Miyamoto, M., Koyama, K., and Ohdaira, K., Sol. Energy Mat. Sol. Cells. 95 (2011) 797.Google Scholar
3. Hayakawa, T., Miyamoto, M., Koyama, K., Ohdaira, K., and Matsumura, H., Thin Solid Films 519 (2011) 4466.Google Scholar
4. Matsumura, H., and Tachibana, H., Appl. Phys. Lett. 47 (1985) 833.Google Scholar
5. Ansari, S. G., Umemoto, H., Morimoto, T., Yoneyama, K., Masuda, A., Matsumura, H., Ikemoto, M., and Ishibashi, K., J. Vac. Sci. Technol. A 23 (2005) 1728.Google Scholar
6. Godlewski, M.D., Baraona, C. R., and Bandhorst, H. W. Jr, Sol. Cells 29 (1990) 131.Google Scholar