Reversible Photoproduction of Stable Charged Defects in Trans-Polyacetylene

Published online by Cambridge University Press:  25 February 2011

Carolyn Hoener
Carolyn Hoener*
Affiliation:
Laboratory of Chemical Biodynamics, Lawrence Berkeley Laboratory, Berkeley, CA
Get access

Abstract

Photoproduction and photodepletion of stable charged defects in trans-polyacetylene were observed, at low temperatures, by monitoring the IR signature of these defects: absorptions at 1368, 1289, 640 cm−1 (1053, 600 cm−1 for (CD)x). These absorptions could be observed at long times (two to several hundred minutes) after photolysis, only when the sample was protected from photolysis by the probe beam, by blocking v > 2,300 cm−1.

The location of these absorptions and the temperature dependence of their intensities were similar to those of previously observed photoinduced defects reported to have much shorter lifetimes (τ - ms). The stable defects reported here can be produced at much lower photolysis energies (v > 5,000 cm−1) than transient-photoinduced defects (v > 9,000 cm−1). A mechanism for the photoproduction of stable defects, involving a two-photon process catalyzed by existing neutral defects, is proposed to explain this low onset.

The slow decay of these defects observed when the sample is kept in the dark is attributed to photoinduced depletion by blackbody irradiation. This process was slow enough to allow the wavelength dependence of photodepletion (observed at 2,800 < v < 8,000 cm−1) to be studied. The photodepletion was fastest near 4,500 cm−1, suggesting that the defects possess an electronic absorption (with a peak near 4,500 cm−1) similar to that observed directly for the transient-photoinduced defects.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 173: Symposium Q – Advanced Organic Solid State Materials , 1989 , 431
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Salem, L., The Molecular Orbital Theory of Conjugated Systems, (W. A. Benjamin Inc., Reading MA, 1974), p. 518 Google Scholar
2 Etemad, S., Heeger, A. J., MacDiarmid, A. G., Ann. Rev. Phys. Chem. 33, 443, (1982)CrossRefGoogle Scholar
3 Etemad, S., Baker, G. L., Roxlo, C. B., Weinberg, B. R., J. Orenstein, Mol. Cryst. Liq. Cryst. 117, 275, (1985)Google Scholar
4 Fujimoto, H., Tanaka, J., Tanaka, M., Bull. Chem. Soc. Jpn 56, 671, (1983)CrossRefGoogle Scholar
5 Su, W. P., Schrieffer, J. R., Proc. Natl. Acad. Sci. 77, 5626, (1980)CrossRefGoogle Scholar
6 Blanchet, G. B., Fincher, C. R., Chung, T. C., Heeger, A. J., Phys. Rev. Letts. 50, 1938, (1983)Google Scholar
7 Rothberg, L., Jedju, T. M., Etemad, S., Baker, G. L., Phys. Rev. Lett. 57, 3229, (1986)Google Scholar
8 Orenstein, J., Baker, G. L., Phys. Rev. B49, 1043, (1982)Google Scholar
9 Flood, J. D., Heeger, A. J., Phys. Rev. B28, 2356, (1983)Google Scholar
10 a) Orenstein, J., Ch. 36, TheHandbook of Conducting Polymers, Skotheim, T. Ed. (M. Dekker, New York, 1986)Google Scholar
b) Colaneri, N. F., Friend, R. H., Schaffer, H. E. Heeger, A. J., Phys. Rev. B38, 3960, (1988)Google Scholar
11 Ito, T., Shirakawa, H., Ikeda, S., J. Polym. Sci., Poly. Chem. Ed. 12, 11, (1974)Google Scholar