Silicon Nitride Coatings Formed using the Selective Area Laser Deposition (SALD) Technique

Published online by Cambridge University Press:  10 February 2011

Lianchao Sun
Affiliation:
Institute of Materials Science, The University of Connecticut, Storrs, CT 06268-3136
Leon L. Shaw
Affiliation:
Institute of Materials Science, The University of Connecticut, Storrs, CT 06268-3136
Harris L. Marcus
Affiliation:
Institute of Materials Science, The University of Connecticut, Storrs, CT 06268-3136
Get access

Abstract

In this paper, the Selective Area Laser Deposition (SALD) technique was used to deposit silicon nitride material from the gas phase. Tetramethylsilane (TMS) and ammonia were chosen as precursors for silicon and nitrogen respectively. Effects of processing temperatures and gas ratios of TMS to total pressure (PTMS + PNH3) on the relative amounts of silicon nitride and the growth kinetics were studied. Further, surface morphology and electrical properties of the deposits were also examined. It is found that the as-deposited materials are mainly composed of amorphous phases and the heat-treated samples (at 1500°C for 8hrs) consist of α-Si 3N4, α-SiC and β-SiC. The amount of αz-Si3N4 decreases with the increase of the TMS pressure. The volume growth rate of deposits also increases with the TMS pressure. The apparent activation energy for these processes is estimated as 1 OOkJ/mol.

Type
Research Article
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Hampshire, S., “Engineering Properties of Nitrides, in Engineering Materials Handbook, Vol.4: Ceramic and Glass,” S. J. Schneieder, Ed. ASM International, 1991, pp804811.Google Scholar
2. Lehmann, O. and Stuke, M., Science, 270, pp16441646, (1996).Google Scholar
3. Wallenberger, F.T, Science, 267, pp1274–5, (1995).Google Scholar
4. Crocker, J. E., Jakubenas, K. J., Harrion, S. and Marcus, H. L., Solid Freeform Fabrication Proceedings, The University of Texas at Austin, 1997, 489496.Google Scholar
5. Sun, L., Jakubenas, K. J., Crocker, J. E., Harrison, S., Shaw, L. L. and Marcus, H. L., Solid Freeform Fabrication Proceedings, The University of Texas at Austin, 1997, 481488 Google Scholar
6. Sun, L., Jakubenas, K. J., Crocker, J. E., Harrison, S., Shaw, L. L. and Marcus, H. L., Materials and Manufacturing Processes, 13, No.6, (1998).Google Scholar
7. Tompkins, J., Ph.D. Dissertation, The University of Texas at Austin, (1998).Google Scholar
8. User's Manual, Bruker Analytical X-ray systems, Bruker AXS Co (Siemens Co.).Google Scholar
9. Wallace, R.W. and Ruh, E., J. of American Ceramic Society, 50, pp.358364, (1967)Google Scholar
10. Rodriguez-Clemente, R., Figueras, A., Garelik, S., Armas, B. and Combescure, C., Journal of Crystal Growth, 125, pp533542, (1992).Google Scholar
11. Herlin, N., Lefebvre, M., Pealat, M. and Perrin, J., J. Phys. Chem. M96, pp70637072, (1992).Google Scholar
12. Figueras, A., Garelik, S., Rodriguez-Clemente, R., Armas, B., Combescure, C. and Dupuy, C., Journal of Crystal Growth, 110, 528542, (1991).Google Scholar
13. Harrison, S. and Marcus, H. L., submitted to J. of American Ceramic Society, (1998).Google Scholar