Strain Rate Effects on Hydrogen Embrittlement Characteristics of Notched 4340 Steel

Published online by Cambridge University Press:  16 May 2014

Mobbassar Hassan Sk  and
Ruel A Overfelt
Mobbassar Hassan Sk
Affiliation:
National Center of Excellence for Research in the Intermodal Transport Environment, Materials Engineering, Auburn University, Auburn, AL 36849, United States Tel.: +1 334 844 5940; fax: +1 334 844 3400, skmobba@auburn.edu , overfra@auburn.edu
Ruel A Overfelt
Affiliation:
National Center of Excellence for Research in the Intermodal Transport Environment, Materials Engineering, Auburn University, Auburn, AL 36849, United States Tel.: +1 334 844 5940; fax: +1 334 844 3400, skmobba@auburn.edu , overfra@auburn.edu
Get access

Abstract

The effect of strain rate on hydrogen embrittlement of low alloy 4340 steel was studied using double-notched tensile samples electrochemically charged in-situ with hydrogen in 1N H2SO4 + 5 mg/l As2O3 solution. The mechanical response of samples with prior austenitic grain sizes of 10 and 40 μm and martensitic hardness of 43-52 HRC were examined after hydrogen charging times of 0-20 min. Increasing the strain rate for hydrogen charged samples resulted in decreased failure strains and increased evidence of brittle fracture. Brittle fracture surfaces for the harder samples showed primarily intergranular fracture while softer samples exhibited predominantly quasi-cleavage.

Keywords

embrittlementgrain boundarieshardness
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1650: Symposium JJ – Materials Fundamentals of Fatigue and Fracture , 2014 , mrsf13-1650-jj04-02
Copyright
Copyright © Materials Research Society 2014 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Kafle, J. and Qu, D., “Enhancement of Hydrogen Insertion into Carbon Interlayers by Surface Catalytic Poisoning”, J. Phys. Chem. C, 11, 19108 (2010)CrossRefGoogle Scholar
Louthan, M R. Jr., “The Effect of Hydrogen on Metals”, Corrosion Mechanism, Fansfield, , Editor Marcel Dekker Inc. NY 1987 Google Scholar
McMahon, C. J. Jr.,“Hydrogen-induced intergranular fracture of steels”, Eng. Fract. Mech. 68, 773 (2001).CrossRefGoogle Scholar
Martin, M., Fenske, A., Liu, G., Sofronis, P., Robertson, I., “On the formation and nature of quasi-cleavage fracture surfaces in hydrogen embrittled steels, Acta Mat., 59, 1601 (2011)CrossRefGoogle Scholar
Nagao, , Smith, C., Dadfarnia, M., Sofronis, P., Robertson, I. “The role of hydrogen in hydrogen embrittlement fracture of lath martensitic steel, Acta Mat. 60, 5182 (2012)CrossRefGoogle Scholar
Lynch, S.P., “Interpreting hydrogen-induced fracture surfaces in terms of deformation processes: A new approach,” Scripta Mat., 65, 851 (2011).CrossRefGoogle Scholar
Krom, A.H.M., Maier, H.J., Koers, R.W.J., Bakker, A., “The effect of strain rate on hydrogen distribution in round tensile specimens”, Materials Science and Engineering A 271, 20(1999)CrossRefGoogle Scholar
ASTM E112-96, “Standard Test Methods for Determining Average Grain Size,” ASTM International (Philadelphia, PA) 1996 Google Scholar
http://www.laboratorydevicesco.com/TENSILES.html Google Scholar
J, Lessar, F. and Gerbarich, W.W, “Grain Size Effects in Hydrogen-Assisted Cracking”, Met. Trans., 4, 953 (1976)CrossRefGoogle Scholar