A Tem Study of Defect Structure in GaAs Film on Si Substrate

Published online by Cambridge University Press:  22 February 2011

Sahn Nahm ,
Hee-Tae Lee ,
Sang-Gi Kim  and
Kyoung-Ik Cho
Sahn Nahm
Affiliation:
Semiconductor Division, Electronics and Telecommunications Research Institute, Daedok Science Town, P.O. Box 8, Daejeon, 305-606, Korea
Hee-Tae Lee
Affiliation:
Semiconductor Division, Electronics and Telecommunications Research Institute, Daedok Science Town, P.O. Box 8, Daejeon, 305-606, Korea
Sang-Gi Kim
Affiliation:
Semiconductor Division, Electronics and Telecommunications Research Institute, Daedok Science Town, P.O. Box 8, Daejeon, 305-606, Korea
Kyoung-Ik Cho
Affiliation:
Semiconductor Division, Electronics and Telecommunications Research Institute, Daedok Science Town, P.O. Box 8, Daejeon, 305-606, Korea
Get access

Abstract

For the GaAs buffer layer deposited on Si substrate at 80°C and annealed at 300°C for 10 min, the size of most GaAs islands was observed as ∼ 10 nm but large islands (∼ 40 nm) were also seen. According to the calculation of spacing of moire fringes, large GaAs islands are considered to be rotated about 4 ° with respect to the Si substrate normal. However, for the main GaAs film overgrown on the GaAs buffer layer at 580 °C, moire fringes with the spacing of 5 nm (GaAs film without rotation) completely covered the surface of Si substrate. Misfit dislocations and stacking faults were already formed at the growth stage of buffer layer. Stacking faults and misfit dislocations consisting of Lomer and 60 ° dislocations were observed in GaAs films grown at 580 °C. However, after rapid thermal annealing at 900 °C for 10 sec, only Lomer dislocations with 1/2[110] and 1/2[-110] Burgers vectors were observed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 325: Symposium L – Physics and Applications of Defects in Advanced Semiconductors , 1993 , 457
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Fang, S. F., Adomi, K., Iyer, S., Morkoc, H., Zabel, H., Choi, C., and Otsuka, N., J. Appl. Phys. 68, R31(1990).CrossRefGoogle Scholar
[2] Koch, S. M., Rosner, S. J., Hull, R., Yoffe, G. W., and Harris, J. S. Jr., J. Crystal Growth, 81, 205 (1987).Google Scholar
[3] Kim, I., M.S. Dissertation, Korea Advanced Institute of Science of Techonology (1992).Google Scholar
[4] Reimer, Ludwig, Transmission Electron Microscopy (Springer-Verlag, Berlin, Heidelberg, New York, Tokyo, 1984).Google Scholar
[5] Nozawa, K., and Horikoshi, Y., Jpn. J. Appl. Phys. 32, 626 (1993).Google Scholar
[6] Choo, W. K., Kim, I., Lee, J. Y., Cho, K. I., Lee, J. L., and Kim, Y. J., Mat. Res. Soc. Symp. Proc. vol. 263, 131(1992).Google Scholar
[7] Cho, K. I., Choo, W. K., Lee, J. Y., Park, S. C., and Nishinaga, T., J. Appl. Phys. 69, 237 (1991).CrossRefGoogle Scholar