Characterization of Type B Carbonate Apatite Sintered Bodies
Published online by Cambridge University Press: 10 February 2011
Abstract
The dissolution kinetics of type B carbonate apatite (CAp) disks sintered at different temperatures were investigated under acidic conditions similar to an osteoclastic desorption process in bone remodeling. The type B CAp disks, which were uniaxially pressed at 98MPa and sintered at temperatures of 600 to 700 ºC, showed single crystalline phase and a high relative density of 60-62 % compared to the stoichiometric density of 3.16g/cm3 of hydroxyapatite (HAp). The dissolution rate of type B CAp disks sintered at 650 ºC was 3.5 times faster than that of HAp disks at 650 ºC. These results indicate that the Type B CAp sintered disks show potential use as a biodegradable material for artificial bone.