The Correlation of Stress-State and Nano-Mechanical Properties in Au

Published online by Cambridge University Press:  10 February 2011

K. F. Jarausch ,
J. D. Kiely ,
J. E. Houston  and
P. E. Russell
K. F. Jarausch
Affiliation:
Department of Materials Science and Engineering, North Carolina State University, Raleigh, NC 27695-7918 Surfaces and Interfaces Department Sandia National Laboratories, Albuquerque, NM 87185-1413
J. D. Kiely
Affiliation:
Surfaces and Interfaces Department Sandia National Laboratories, Albuquerque, NM 87185-1413
J. E. Houston
Affiliation:
Surfaces and Interfaces Department Sandia National Laboratories, Albuquerque, NM 87185-1413
P. E. Russell
Affiliation:
Department of Materials Science and Engineering, North Carolina State University, Raleigh, NC 27695-7918
Get access

Abstract

A dependence of elastic response on the stress-state of a thin-film has been demonstrated using the interfacial force microscope (IFM). Indentation response was measured as a function of the applied biaxial stress-state for 100 nm thick Au films. An increase in measured elastic modulus with applied compressive stress, and a decrease with applied tensile stress was observed. Measurements of elastic modulus before and after applying stress were identical indicating that the observed change in response is not due to a permanent change in film properties.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 522: Symposium T – Fundamentals of Nanoindentation & Nanotribology , 1998 , 119
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] LaFontaine, W. R., Paszkiet, C. A., Korhonen, M. A., Li, Ghe-Yu, J. Mater. Res. 6 (1991) 2084.Google Scholar
[2] Vanlandingham, M. R., Knight, S. H., Palmese, G. R., Elings, J. R., Huang, X., Bogetti, T. A., Eduljee, R. F., and Gillespie, J. W. Jr, In press.Google Scholar
[3] Tangyungong, P., Thomas, R. C., Houston, J. E., Michalske, T. A., Crooks, R. M., Howard, A. J., Phys. Rev. Lett. 71 (1993) 3319.Google Scholar
[4] Strojny, A., Gerberich, W. W., Submitted to MRS Bulletin, Proceedings from Spring MRS'98.Google Scholar
[5] Tsui, T. Y., Oliver, W. C., Pharr, G. M., J. Mater. Res., 11 (1996) 752.Google Scholar
[6] Bolshakov, A., Oliver, W. C., Pharr, G. M., J. Mater. Res., 11 (1996) 760.Google Scholar
[7] Denver Instruments XE-50Google Scholar
[8] Sneddon, I. N., Int. J. Engng Sci. 3 (1965) 47.Google Scholar
[9] Russell, P. E., Stark, T. J., Griffis, D. P., Phillips, J. R., Jarausch, K. F., Submitted to J.V.S.T., Proceedings from 1997 Japan-USA Seminar on the Formation of Ion Nanobeams and Applications to Materials Processing.Google Scholar
[10] JEOL 6400FEGoogle Scholar
[11] NT-MDT, www.ntmdt.ruGoogle Scholar
[12] Shenderova, O., Mewkill, P., Brenner, D. W., Jarausch, K., Russell, P. E., Submitted to MRS Bulletin, Proceedings from Spring MRS'98.Google Scholar