Improved Performance in Monofilament Fiber Reinforced Glass Matrix Composites Through the Use of Fiber Coatings

Published online by Cambridge University Press:  21 February 2011

William K. Tredway  and
Karl M. Prewo
William K. Tredway
Affiliation:
United Technologies Research Center, Silver Lane, East Hartford, CT 06108
Karl M. Prewo
Affiliation:
United Technologies Research Center, Silver Lane, East Hartford, CT 06108
Get access

Abstract

The mechanical performance of glass matrix composites reinforced with large diameter (140 µm) monofilaments has been investigated. Strong interfacial adhesion between uncoated boron monofilaments and the borosilicate glass matrix resulted in composites exhibiting low failure strain and brittle fracture. The use of coated monofilaments improved composite performance considerably by reducing fiber-matrix interfacial adhesion. Auger analysis of the interface indicated that a carbon-rich layer had formed between the monofilament coating and the matrix during composite fabrication

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 170: Symposium N – Interfaces in Composites , 1989 , 215
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Crivelli-Visconti, I. and Cooper, G. A., Nature 221, 754 (1969).Google Scholar
2. Sambell, R. A. J., Bowen, D. H. and Phillips, D. C., J. Mater. Sci. 7, 663 (1972).Google Scholar
3. Phillips, D. C., J. Mater. Sci. 2, 1847 (1974)Google Scholar
4. Prewo, K. M., UTRC Internal Report No. R79-111330-6, 1979.Google Scholar
5. Prewo, K. M., Bacon, J. F. and Dicus, D. L., SAMPE Quart. 10, 42 (1979)Google Scholar
6. Prewo, K. M., J. Mater. Sci. 17, 3549 (1982).Google Scholar
7. Prewo, K. M., J. Mater. Sci. 21, 3590 (1986).Google Scholar
8. Brennan, J. J., in Interfacial Characterization of Glass and Glass-Ceramic Matrix/Nicalon SiC Composites, edited by Tressler, R. E., Messing, G. L., Pantano, C. G. and Newnharn, R. E. (Plenum Press, New York, 1986) pp. 549.Google Scholar
9. Nardone, V. C. and Prewo, K. M., J. Mater. Sci. 23, 168 (1988).Google Scholar
10. Prewo, K. M., Johnson, B. and Starrett, S., J. Mater. Sci. 24, 1373 (1989).Google Scholar
11. Jarmon, D. C. and Prewo, K. M., ONR Report No. R86-917054-1, 1986.Google Scholar
12. Cooper, R. F. and Chyung, K., J. Mater. Sci. 22, 3148 (1987).Google Scholar
13. Brennan, J. J., AFOSR Report No. R89-917894-1, 1989.Google Scholar