Structures and Mechanical Properties of ECAP Processed 7075 Al Alloy upon Natural Aging and T651 Treatment

Published online by Cambridge University Press:  15 March 2011

Yonghao Zhao ,
Xiaozhou Liao ,
Ruslan Z. Valiev  and
Yuntian T. Zhu
Yonghao Zhao
Affiliation:
Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, NM-87545, U.S.A.
Xiaozhou Liao
Affiliation:
Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, NM-87545, U.S.A.
Ruslan Z. Valiev
Affiliation:
Institute of Physics of Advanced Materials, Ufa State Aviation Technical University, 12 K. Marx Street, 450000 Ufa, RussianFederation
Yuntian T. Zhu
Affiliation:
Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, NM-87545, U.S.A.
Get access

Abstract

Equal-channel angular pressing (ECAP) processed ultrafine grained (UFG) and coarse grained (CG) 7075 Al alloys were treated by natural aging and T651 temper (annealed at 120 °C for 48 h in Ar atmosphere), respectively. Mechanical tests showed that for the UFG sample, the natural aging resulted in the highest strength (the ultimate tensile strength is 720 MPa). In contrast, for the CG sample, the T651 treatment resulted in a higher strength (the ultimate strength is 590 MPa) than the natural aging (530 MPa). Microstructural analyses indicated that the enhanced strength of the T651 treated CG sample was mainly caused by high densities of G- P zones and metastable η' precipitates. The enhanced strength of the naturally aged UFG sample was mainly caused by the high densities of G-P zones and dislocations. Upon T651 treatment, the dislocation density of the UFG sample deceased significantly, overcompensating the precipitation strengthening.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 821: Symposium P – Nanoscale Materials & Modeling-Relations Among Processing, Microstructure and Mechanical Properties , 2004 , P9.9
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Valiev, R.Z., Islamgaliev, R.K. and Alexandrov, I.V., Prog. Mater. Sci. 45, 103 (2000).Google Scholar
2. Wang, J., Iwahashi, Y., Horita, Z., Furukawa, M., Nemoto, M., Valiev, R.Z. and Langdon, T.G.. Acta mater. 44, 2973 (1996).Google Scholar
3. Furukawa, M., Utsunomiya, A., Matsubara, K., Horita, Z. and Langdon, T.G., Acta mater. 49, 3829 (2001).Google Scholar
4. Lee, S., Utsunomiya, A., Akamatsu, H., Neishi, K., Furukawa, M., Horita, Z. and Langdon, T.G., Acta mater. 50, 553 (2002).Google Scholar
5. Morris, D.G. and Munoz-Morris, M.A., Acta mater. 50, 4047 (2002).Google Scholar
6. Horita, Z., Fujinami, T., Nemoto, M. and Langdon, T.G., Metall. Trans. 31A, 691 (2000).Google Scholar
7. Zheng, L.J., Chen, C.Q., Zhou, T.T., Liu, P.Y. and Zeng, M.G., Mater. Character. 49, 455 (2003).Google Scholar
8. Smith, W.F., Structure and Properties of Engineering Alloys, (McGraw-Hill: New York, 1993) Chap. 5-9, p. 214.Google Scholar
9. Murakami, Y., Aluminum-Based Alloys, in Processing Metals and Alloys, edited by Cahn, R.W. (VCH: Weinheim, New York, c1991), p. 253.Google Scholar
10. Zhao, Y.H., Liao, X.Z., Jin, Z., Valiev, R.Z. and Zhu, Y.T., in Ultrafine-Grained Materials III, edited by Zhu, Y.T., Langdon, T.G., Valiev, R.Z., Semiatin, S.L., Shin, D.H. and Lowe, T.C. (The Minerals, Metals & Materials Society, 2004), p. 511.Google Scholar
11. Zhao, Y.H., Zhang, K. and Lu, K., Phys. Rev. B, 56, 14322 (1997).Google Scholar
12. Zhao, Y.H., H.W. Sheng and Lu, K., Acta mater. 49, 365 (2001).Google Scholar
13. Zhao, Y.H., Zhang, K. and Lu, K., Phys. Rev. B, 66, 085404–01 (2002).Google Scholar
14. Zhao, Y.H., Liao, X.Z., Jin, Z., Valiev, R.Z. and Zhu, Y.T., to be published in Acta mater. (2004).Google Scholar