Introduction
In 2018, excavations by the University of Sheffield on the Migration Period cemetery at Scremby, Lincolnshire, revealed a grave containing a copper-alloy enamelled cup as part of its assemblage. The cup came from a burial dated to the first half of the sixth century, one of forty-nine inhumation burials in the cemetery. The vessel accompanied an adolescent female, in a sparsely furnished grave: besides the cup, only two plain annular brooches and a pair of simple wrist clasps were found.
Although the burial dates to the sixth century ad, the cup is Roman and thus of considerable age when deposited. Several similar Roman enamelled vessels are known from antiquarian investigations in the UK, and in recent years hobby metal detectorists have added to the corpus. The Scremby Cup, however, is one of very few such vessels found during a modern excavation and from a secure archaeological context. This find provides the opportunity to examine a new and significant addition to this corpus of Roman metalwork, both stylistically and compositionally. Furthermore, its location in an Anglo-Saxon grave and the results from residue analysis of its contents demand consideration of what function and meanings it might have held for an audience that was very different from that originally intended. How the cup survived and changed course over three centuries are key aspects of our enquiry, demonstrating the importance of studying an artefact's biography rather than just viewing it through a static, typological lens.
The Funerary Context
The cup came from a burial at Scremby (Lincolnshire). The site consisted of forty-nine richly furnished inhumation burials, all interred between c. ad 480 and 540, and containing a range of grave goods typical for a Migration Period cemetery in that part of eastern England. Although a few fragments of Roman material were present in some of the other graves, a phenomenon well-attested in burials of this period (see below), the inclusion of a complete and still usable cup was unique at this site, and a rare occurrence nationally.
The vessel was found beside the head of an adolescent female (Sk18), aligned west-east, her body flexed and the head and knees facing north (Figure 1). Her grave was unusually sparsely furnished compared to the other female burials at Scremby. It contained no beads, belt, or bag, the only other artefacts being two plain annular brooches (Hines, Reference Hines1984: 260–67) and a pair of simple Hines Type B wrist clasps (Hines, Reference Hines1993: 90–92). Such finds are ubiquitous in sixth-century graves in Lincolnshire, with annular brooches occurring in around ninety per cent of female burials in the region (Leahy, Reference Leahy2007: 64). Of the cemetery's other twenty-nine female burials that were sufficiently undisturbed by later agricultural activity, only two contained fewer artefacts in their assemblages.
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig1.png?pub-status=live)
Figure 1. Burial Sk18 from Scremby (Lincolnshire).
The cup nevertheless clearly held significant meaning for the deceased and the people who performed the funerary rites. Not only was it placed prominently by the head of the deceased, but also it was an intact and still functional vessel. In this regard, it differs from other pieces of occasional Roman metalwork found in the Scremby burials, which are pieces of scrap whose original purpose has long been lost. The cup, in contrast, was still a viable container.
Form, Decoration, and Provenance of the Cup
The Scremby Cup is 57 mm tall and gently convex-sided; its walls are between 1 and 1.5 mm thick, with a slightly rounded and in-turned rim, whose diameter is 97 mm (Figure 2). The base is made from a separate extremely thin metal sheet around 0.5–0.8 mm thick and 58 mm in diameter, soldered onto the cup's body. The fact that the cup retains its base, although highly fragmented, is unusual, as vessels of a similar form and construction found in antiquarian investigations or by metal detecting are almost invariably missing this element. A notable exception is a cup found in the nineteenth century at Rochefort-sur-Nenon (Jura, France), which also has a thin separate base piece soldered onto the main body (Pelpel & Vernou, Reference Pelpel and Vernou2018: 251, fig. 2).
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig2.png?pub-status=live)
Figure 2. The Scremby Cup.
When complete, the Scremby Cup would have held around 280 ml of liquid. Its body is decorated with vertical panels of cast insets, most of which retain the remains of coloured enamels in aquamarine, red, and deep blue/purple. Since considerable attention has been paid to cataloguing and classifying the corpus of Roman enamelled vessels in the UK and continental Europe in recent years (e.g. Künzl, Reference Künzl and Mols1995; Breeze, Reference Breeze2012a; Pelpel & Vernou, Reference Pelpel and Vernou2018; Grossi, Reference Grossi2020), it is not our intention to revisit this work here. While these and other publications have served to highlight vessels comparable in form and decoration, there is no direct comparison for the Scremby Cup among this group. It is worth noting, however, that relatively few enamelled vessels have been found during modern archaeological excavations. Exceptions in Britain include a flask dating to the first half of the second century ad from Corbridge, Northumberland (Casey & Hoffmann, Reference Casey and Hoffmann1995: 24), and pans from the sacred spring at Bath, Somerset (Henig et al., Reference Henig, Brown, Baatz, Sunter, Allason-Jones, Cunliffe and Davenport1988: 9–21), and the cemetery at Brougham, Cumbria (Cool, Reference Cool2004: 124–28). Despite their archaeological scarcity, new finds of enamelled vessels are still being made in Britain by hobby metal detectorists, most recently at St Lavan, Cornwall, in 2019 (Pearce & Worrell, Reference Pearce and Worrell2020).
To date, most British enamelled vessels are either cups or pans, although the latter are considerably more common. Ostensibly the forms are the same, the key difference being the presence of a flat horizontal handle in the case of a pan. The three so-called ‘Hadrian's Wall Series’ vessels (as they are decorated with the names of military forts on the frontier), the Rudge Cup, Amiens Patera, and Ilam Pan, share their body shape: a convex side and an in-turned rim (Breeze, Reference Breeze and Breeze2012b). They are also squat, with the overall height of the vessel being less than the base diameter. A similar shape and body proportion can be seen in the Winterton (Lincolnshire) and Eastrington (East Yorkshire) pans (British Portable Antiquities Scheme, hereafter PAS: PAS NLM-F50443 and PAS YORKM-20B68C), which are so alike in appearance that they almost certainly came from the same workshop. The Scremby Cup, in contrast, is subtly different; it has a taller profile and, although it is still slightly convex-sided, this is much less pronounced, and the rim remains the widest portion of the vessel.
One of the closest parallels for the slightly taller, less convex shape of the Scremby Cup is the Selborne Cup, found in Hampshire in 1867, with which it shares some stylistic similarities (Grossi, Reference Grossi2020: 216). It is a handled barrel-shaped beaker formed from two identical cups, one inverted over the other and soldered in place, although they have long since become separated. There is no suggestion that the Scremby Cup was part of a larger composite vessel; its rounded rim is very well preserved and polished, and there is no evidence of a soldered join, unlike on the base. There is also no indication that a horizontal handle was ever attached to the rim (which would make it a pan). Indeed, the Scremby vessel lacks the slight but pronounced foot often seen on handled vessels such as the Ilam and Amiens pans (Breeze, Reference Breeze2012a: 2; Jackson, Reference Jackson and Breeze2012: 43). Consequently, we are confident that it is a handle-less cup.
The cup is ornamented with inset motifs that were cast into the vessel's surface, before being infilled with coloured enamelling. It is particularly distinctive for the arrangement of its design into vertical rather than horizontal panels, as is usual on pans and cups found in British contexts. Two alternating panels are present (Figure 3). The first consists of seven shields, or half-moons, flanked on either side by five inward-turned trumpets. The second is formed from a column of four hearts, or stylized palmettes, with flanking triangular infills. These sit atop a single horizontal panel of inverted elongated triangles above the base. The insets are filled with red, aquamarine, and deep blue/purple glass and, although generally these are in an alternating pattern, sometimes certain colours appear together in adjacent cells.
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig3.png?pub-status=live)
Figure 3. Cross-section of the cup and its decorative scheme.
Parallels for this decorative arrangement, or even individual elements within the scheme, are hard to find within the British corpus. A somewhat cruder version of a trumpet design appears within the crenelated gaps of the Rudge Cup (Allason-Jones, Reference Allason-Jones and Breeze2012: 23) but, beyond this, there are few similarities between the two vessels. Likewise, no real parallels exist in the assemblage of mould fragments excavated at Castleford in Yorkshire. Among this waste from the manufacture of cast enamelled copper-alloy vessels dated to c. ad 85–95, only two mould fragments, Pattern 9 and Pattern 12, have an element in common with the Scremby Cup, namely the stylized heart; otherwise, they are stylistically entirely different (Bayley & Budd, Reference Bayley, Budd, Cool and Philo1998: 212–13). Moreover, all the moulds from Castleford were for creating horizontal designs and not vertical panels. Only one vessel from Britain shares more than a single design element, the Selborne Cup mentioned earlier (Grossi, Reference Grossi2020: 126). This vessel has trumpet and heart-shaped cells, along with triangular infills, although these are arranged in a continuous mosaic pattern rather than in distinct and ordered panels.
Closer parallels for the decorative scheme of the Scremby Cup can be found on three vessels with a French provenance. The best known is a vase, now in the Metropolitan Museum of Art (Inv. 47.100.5), found at La Guierce (Charente) in 1849 (Figure 4), where it had been deposited containing a hoard of coins dating to ad 260–70 (Forsyth, Reference Forsyth1950: 303–07). It is a composite vessel formed from two main elements, the lower portion being cup-shaped. The body of this vessel is decorated with two alternating vertical panels. The first is very similar to Scremby and consists of inward-facing trumpets. The second consists of a pelta pattern, not precisely the same but still quite close to the hearts on the Scremby Cup. Like Scremby, the enamelling is in red, deep blue, and aquamarine.
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig4.png?pub-status=live)
Figure 4. Vase from La Guierce (Charente, France). Reproduced by permission of the Metropolitan Museum of Art, New York.
Another composite vessel with close parallels to the Scremby Cup is a complex flask or ‘wine thief’ from Ambleteuse in the Pas-de-Calais (Figure 5), recovered in the early nineteenth century in association with coins of Emperor Tacitus (ad 275–76) and now in the British Museum (BM 1843, 0623.1). This vessel's form and function has recently been re-evaluated (Bailey, Reference Bailey and Entwistle2003). Although arranged very differently, the body of this vessel, and its lower portion are decorated with patterns of hearts, shields, and infilled triangles, again in vertical panels. Although most of the original enamel has long since disappeared, a few surviving elements indicate that the cells were infilled with red and deep blue glass.
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig5.png?pub-status=live)
Figure 5. Complex flask or ‘wine thief’ from Ambleteuse (Pas-de-Calais, France). Reproduced by permission of the Trustees of the British Museum.
A final parallel is a cup now in the Musée d'Archéologie nationale in Saint-Germain-en-Laye (Inv. 31672). Although unprovenanced, it is likely to be a French find, and its shape is remarkably similar to the Scremby Cup. The principal scheme revolves around decorative roundels, with the space between these filled with trumpets and hearts almost identical to those on the Scremby Cup (Forsyth, Reference Forsyth1950: fig. 14; Grossi, Reference Grossi2020: 127).
It is possible to reach some cautious conclusions concerning the origins of the Scremby Cup and its original function. While it is tempting to suggest a British origin, based on the concentration of enamelled vessels found in central and eastern England, it differs from all other examples in its form and decoration. Somewhat better, if by no means exact, parallels can be found with vessels recovered in France, suggesting a possible origin on the European continent. If the association of two of the French examples with coins of ad 260–70 is to be trusted, a date of manufacture around the third quarter of the third century can tentatively be proposed. This is somewhat at odds with the late first to early second-century date usually given to such vessels in Britain; such dating is, however, sometimes based on little contextual evidence (e.g. Moore, Reference Moore1978: 235; Künzl, Reference Künzl and Breeze2012: 18). The cup's original function is, perhaps, easier to define. Hunter (Reference Hunter and Breeze2012: 92–94) has highlighted the clear association between both pans and cups and drinking. This seems to be confirmed by a fragment of enamelled pan handle from Gunthorpe (Norfolk), which incorporates the motto bebe sese (drink – live long) within its decorative scheme (PAS NMS-7BC635).
Method of Production and Composition
A microscopic materials analysis of fragments of the body and base of the cup were undertaken using a Leica DM 2700P polarized microscope and a Hirox RH-2000 3D digital system. The grain structure clearly shows that both the body and base of the cup were cast and not subsequently worked, beyond fine finishing, as the grains are well formed and there is no evidence of twinning or other grain distortion (Scott, Reference Scott1991: 8–9) (Figure 6a). Intergranular corrosion is also visible in the cup's body and base (Figure 6b).
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig6.png?pub-status=live)
Figure 6. a) The grain structure of the base of the cup shows no indication that the cast metal has been subsequently worked. Image originally captured at 1000× magnification. b) The grain structure of the base of the cup shows no indication that the cast metal has been subsequently worked. Additionally, intergranular corrosion is visible throughout. Image originally captured at 400×.
Three-dimensional imaging, using an Artec Spider (providing point accuracy of up to 0.05 mm and with texture removed), clearly showed striations on the outer surface of the cup, suggesting that the exterior of the artefact had been polished after casting and before adding the enamel, which has been applied in a champlevé technique (Dolfini & Crellin, Reference Dolfini and Crellin2016; Crellin, Reference Crellin2018: 866–67; Barnes, Reference Barnes2019) (Figure 7a–b). The inside of the cup was not polished and retains a rough surface indicative of the surface of the mould used to create it. No casting lines are visible on the interior and, as previously noted, there is no indication that a handle or other attachment had been fixed or soldered to the cup's body. Furthermore, the 3D analysis also suggests that the cup has not been repaired or suffered pre-depositional damage; most of the wear visible on the cup, such as the evident surface corrosion and mineralization, resulted from prolonged exposure to the burial environment, rather than wear while in use.
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig7.png?pub-status=live)
Figure 7. Artec Spider 3D scan view of the cup. a) Exterior showing polishing striations. b) Interior, which has not been polished.
Two possible bronze casting strategies consistent with known Roman practices could have been used to create the cup's body. A lost wax or investment process is possible, where a wax version of the cup's body was crafted around a solid inner core and coated in clay layers. The wax would have been melted out of the mould, and bronze poured into the space, leaving no casting seams on the cup's surface. Alternatively, a mirror of the outside surface pattern of the cup was carved or stamped into clay pieces that were then fitted around an inner core as a multi-part mould; this would usually result in visible casting seams (Bayley & Budd, Reference Bayley, Budd, Cool and Philo1998: 207; Crellin, Reference Crellin2018: 861). As discussed, the design on the cup's body is in vertical panels above a single horizontal panel of inverted elongated triangles circling its base. The spaces between each vertical panel do not easily line up with spaces between the elongated triangles surrounding the bottom, and there is no visible evidence that the pattern of elongated triangles has been interrupted. These details suggest that the cup was created by lost wax technique; a multi-part clay mould would require the decorative spacing between the vertical top panels and horizontal bottom panel to line up to avoid an interruption in the overall pattern.
The base of the cup, a very thin circular disk of bronze, was soldered onto the body with lead, after the cup had its enamel applied. The base was added later because the metal making up the body of the cup expanded and contracted as it was heated and cooled during the champlevé enamelling process (Barnes, Reference Barnes2019: 37). Micrographic analysis of the base shows a higher concentration of slag and other impurities from casting on one side of the base's surface. These impurities generally accumulate at the top of a melt's surface, indicating that the base of the cup was created using a horizontal mould (Scott, Reference Scott1991: 92) (Figure 8a and 8c). Furthermore, the smaller grain structure of the base suggests a faster cooling process (Scott, Reference Scott1991: 5). Together this suggests that an open-cast process with a horizontal circular mould was used to create the base.
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig8.png?pub-status=live)
Figure 8. a) Cross-section view of the base of the cup, showing the casting impurities accumulated on one side of the cast surface. Image originally captured at 400× magnification. b) Image of the body of the cup showing high distribution of lead globules, visible as round grey inclusions, spread throughout the alloy. Original image captured at 350× magnification. c) A darkfield image showing red and green corrosion on the base of the cup, indicating that copper leaching has occurred. Additionally, it is possible to see that the casting impurities have accumulated on one side of the base's surface. Image originally captured at 100× magnification.
The body and base of the cup have been characterized using a portable ThermoScientific Niton XL3t-980 GOLDD X-ray florescence (pXRF) device (Table 1; Supplementary Material 1). The quantities of lead detected in both the body and base of the artefact were well above the solubility level of lead within copper at approximately 8 wt% (Davis, Reference Davis2001: 34–35; NIST, 2013). The presence of lead in quantities of up to 5 wt% benefited the casting process as it acted as a lubricant and improved plasticity, allowing the metal to fill the cast more efficiently while allowing the gas to escape (Davis, Reference Davis2001: 46-51). However, copper and bronze have a higher melting point than lead, and as a leaded copper alloy cools and solidifies, any lead that has not mixed into the melt accumulates at grain boundaries and solidifies into lead globules. The size and number of these globules depends on how much lead was added to the alloy (Scott, Reference Scott1991: 24; Davis, Reference Davis2001: 46–51; NIST, 2013). The high levels of lead detected by pXRF and the presence of multiple lead globules visible at the grain boundaries of the cup suggest that the metalworkers who created this vessel deliberately added a significant amount of lead to the melt mixture (Figure 8b). It is also possible that deposits on the metal's surface, such as trace amounts of solder or the presence of corrosion, have contributed to the observed lead levels in excess of the element's solubility limit in copper alloys (Moffatt et al., Reference Moffatt, Sirois and Miller1997).
Table 1. Handheld portable XRF analysis of the cup's body and base. ND: not detected.
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_tab1.png?pub-status=live)
Arsenic was detected in the bronze in amounts between 1 and 2 wt%. Arsenic increased the metal's hardness and improved a bronze alloy's toughness (Charles, Reference Charles1967: 23; Lechtman, Reference Lechtman1996: 492). The addition of tin, up to 8 wt%, produced a stronger and harder metal with improved ductility and corrosion resistance, qualities that are directly linked to the amount of tin present within the alloy mixture (Lechtman, Reference Lechtman1996: 502). However, above 8 wt%, the alloy becomes brittle (Budd & Ottaway, Reference Budd, Ottaway, Budd, Chapman, Jackson, Janaway and Ottaway1991: 132; Lechtman, Reference Lechtman1996: 502). The red and green corrosion visible on the surface of the samples indicates that the cup has spent a significant amount of time buried, and that some of the copper had leached during this time, leaving a tin-rich corrosion phase. The levels of tin identified in the body and base of the cup thus appear greater than is likely to have been present in the original object (Oudbashi, Reference Oudbashi2015: 1138) (Figure 8c).
The alloy composition employed to produce the cup would have offered advantages, namely the improved castability provided by the lead, the increased hardness offered by the arsenic and tin, and the corrosion resistance of the tin (Lechtman, Reference Lechtman1996: 492–502; Davis, Reference Davis2001: 46–51). The various reasons for the elevated levels of arsenic and tin observed in the Scremby Cup's chemical composition range from the use of arsenical ores, metal recycling processes, and the intentional introduction of alloy elements by the metalworkers who prepared the melt.
While Roman metalworkers would not have been able to easily control the precise amounts of alloying elements they introduced into their work, the specific elements and quantities detected suggest that they understood the value and benefit of alloying from a craft, production, and usage standpoint. The cup's elemental composition also suggests a broad timeframe and region for the artefact's manufacture. The trace amounts of zinc in the quaternary leaded gunmetal alloy (Cu-Sn-Pb-Zn) that makes up the body of the cup are consistent with the alloys being produced in Roman Britain in the third century ad. The mix of elements is also consistent with the Roman practice of recycling metals, which resulted in mixed compositions, as seen in the Scremby Cup (Dungworth, Reference Dungworth1997; Pollard et al., Reference Pollard, Bray, Gosden, Wilson and Hamerow2015: 703). The presence of antimony is particularly associated with Roman copper alloys, and although the presence of silver and antimony together in leaded alloys is common, Blades (Reference Blades1995) suggests that over eighty per cent of Romano-British copper alloys can be characterized by a solo antimony marker. Therefore, the composition of the Scremby Cup, which contains no detected silver, suggests that it may have been manufactured in Britain, although other centres in the north-western Roman empire cannot be ruled out (Bray, Reference Bray, Duckwork and Wilson2020: 245–50).
Organic Residue Analysis
Micro-excavation of the cup's interior during conservation revealed organic residue in the lowest levels of the soil just above the base. One sample of this material underwent organic residue analysis, along with a soil sample from the immediate burial environment as a control. To determine the origin of this residue, absorbed lipids were extracted from both sample residue and soil sample (~300 mg) using an acidified methanol extraction, following Correa-Ascencio and Evershed (Reference Correa-Ascencio and Evershed2014), and characterized by gas chromatography mass spectrometry (GC-MS) (Supplementary Material 2).
After acidified methanol extraction, the residue sample yielded a relatively high concentration of lipids (38165.18 μg g-1), with a value of 5 μg g-1 being deemed the lowest lipid concentration that can be reliably interpreted in archaeological samples (Evershed, Reference Evershed2008). The soil sample, collected from the immediate burial environment, was also extracted using acidified methanol and yielded much lower concentrations of lipids than the organic sample (46.7 μg g-1). This gives confidence that the high concentration of lipids in the sample is not due to contamination from the burial environment. GC-MS revealed a simple lipid profile comprised mainly of saturated fatty acids. This profile is typical of degraded animal fats characterized by an equal dominance of palmitic (C16:0) and stearic acids (C18:0) in addition to relatively low concentrations of unsaturated fatty acids (C18:1), minor odd-chain branched fatty acids (C15:0 and C17:0), and a series of short-chain α,ω-dicarboxylic acids (diacids), ranging from carbon lengths C7 to C10 (Figure 9a).
![](https://static.cambridge.org/binary/version/id/urn:cambridge.org:id:binary:20240529185155271-0181:S1461957124000123:S1461957124000123_fig9.png?pub-status=live)
Figure 9. a) Total ion chromatogram (TIC) of the residue sample acid extract. This chromatogram shows the main fatty acids identified, diacids refer to α,ω-dicarboxylic acids, and the internal standard (IS). The δ13C values, obtained using GC-C IRMS, of C16:0 and C18:0 fatty acids are also shown. b) Plot of Δ13C against δ13C16:0. Values less than −3.3‰ are typically associated with ruminant dairy fats, values between −3.3‰ and −1.0‰ are associated with ruminant adipose and above −1.0‰ can be considered as non-ruminant fats (Dudd & Evershed, Reference Dudd and Evershed1998; Copley et al., Reference Copley, Berstan, Dudd, Docherty, Mukherjee and Straker2003).
To further understand the origin of these lipids, the extract was analysed by gas chromatography-combustion isotope ratio mass spectrometry (GC-C IRMS) to determine the stable carbon isotope value of the major fatty acids (C16:0 and C18:0) (Supplementary Material 2). The Δ 13C value (δ13C18:0 - δ13C16:0) of the residue sample is shown against the approximate range for modern porcine, ruminant carcass, and dairy fats (Figure 9b) (Dudd & Evershed, Reference Dudd and Evershed1998; Copley et al., Reference Copley, Berstan, Dudd, Docherty, Mukherjee and Straker2003). The Δ13C value > -1.0 ‰ indicates a non-ruminant fat source and the enriched δ13C16:0 (-27.24‰) value is typical of a porcine fat origin (Copley et al., Reference Copley, Berstan, Dudd, Docherty, Mukherjee and Straker2003). Mixtures of organic contents can skew these values, but there is no clear evidence of mixing in the absence of other biomarkers.
A significant deposit of pig fats within the cup confirms it retained an active role as a container. Traditionally, when containers, usually in ceramic, have been encountered in Anglo-Saxon burials, they are thought to have held food offerings, and the survival of pig fats might on first inspection suggest the presence of a particularly meat-rich stew. In the absence of characteristic heating markers in the lipid profiles (Supplementary Material 2), it is not possible to confirm whether these fats sustained heating indicative of cooking or not. However, if raw fats were indeed the original contents, then products other than cooked foods can be considered.
The analysis of the contents of a second-century ad Roman cosmetic container from London demonstrated the use of ruminant (cattle/sheep) fats within the preparation of what was interpreted as a ‘moisturiser’ (Evershed et al., Reference Evershed, Berstan, Grew, Copley, Charmant and Barham2004), although a similar cosmetic function for the contents of the Scremby Cup seems doubtful, given the lack of cosmetic ingredients other than fat. It is more likely that the fat had a medicinal purpose. The sixth-century Byzantine physician Anthimus observed that raw bacon fat was considered beneficial by the Franks for bowel and intestinal complaints and the expulsion of worms; he also noted that raw bacon placed on wounds was believed to cleanse putrefaction and speed healing (Grant, Reference Grant1996: 57). While the uncritical transposition of this sixth-century Frankish practice into an English context would be simplistic, it nonetheless remains a tantalizing possibility.
Biography of the Cup
The incidence of Roman and earlier material in Anglo-Saxon graves is a well-documented phenomenon, first comprehensively outlined by White (Reference White1988, Reference White and Southworth1990) and re-evaluated more recently (Werthmann, Reference Werthmann2020). While discussion in the Anglophone world has primarily focused on early Anglo-Saxon cemeteries, this is far from a uniquely British phenomenon. Martin (Reference Martin, Friesinger and Stuppner2004) has observed the frequent presence of Roman coins in Merovingian burials, reused as amulets, placed in belt bags and even the mouths of the dead. Excavations of Migration Period cemeteries in continental Europe have also often encountered burials that contain intact Roman vessels. For example, the sixth- to early seventh-century cemetery at Rosmeer in Limburg (Belgium) revealed graves furnished with complete Roman coarseware bowls and even a complete glass prismatic bottle, all several centuries old upon their final deposition (Roosens & Janssens, Reference Roosens and Janssens1978: 10).
Such Roman items are commonly interpreted as objects put to new uses or repurposed in the early medieval period by people who had no former connection to them. White (Reference White and Southworth1990: 146) suggests that the choice to reuse existing material culture was made primarily for functional reasons; Roman objects could make suitable replacements for items already in use in the Anglo-Saxon milieu. While that may have been the case with objects that could still fulfil their original purpose or be easily modified, most Roman metalwork found in Anglo-Saxon graves consists of partial or fragmented pieces. In some cases, such as in the use of pierced coins incorporated into necklaces, there was still a clear decorative, if non-functional, reason to do so.
For the less diagnostic scrap, other explanations are required. A more ritualistic explanation for the presence of Roman objects in Anglo-Saxon burial assemblages was proposed by Meaney (Reference Meaney1981: 115). She suggested that a more amuletic or apotropaic function might be inferred when old items were found in association with other naturalistic elements such as fossils; these items were often contained in female bag assemblages, an argument developed by Dickinson (Reference Dickinson and Carver1993) in her discussion of a so-called ‘cunning woman’ from Bidford-on-Avon. Both aspects are present in the Scremby Cup: it was still clearly a functional object, but its placement in the ritual context of a burial meant that it must have been imbued with some symbolic value, further enhanced by its distinctive ‘otherness'.
As to how the cup might have been acquired in the sixth century, the condition of the cup may offer a clue. Despite the density in Lincolnshire of Roman remains known to have survived into the early medieval period, albeit in ruinous state (see Green, Reference Green2020: 25–36), the condition of the cup suggests that it was not a casual and fortuitous find recovered from the ploughsoil or debris of a decayed building. This was already recognized by Eckardt and Williams (Reference Eckardt, Williams and Williams2003: 159), who stated that the ‘recovery of complete (Roman) pots or metal objects probably relied on the opening of more closed contexts: hoards and graves’. If we follow this line of argument, while a grave or a hoard are both possibilities for the Scremby Cup, a burial would seem the more plausible. In such a scenario, it would have been actively sought (‘scavenged’?) before being deposited for a second time during the funerary ritual.
When considered in its immediate context, any meanings and values the cup may have held are complex to define. The presence of metal, or occasionally glass, vessels might be assumed to indicate a higher-status burial since they are a comparatively rare grave good during the sixth century (Lucy, Reference Lucy2000: 55–57), but such simplistic high-status attribution is contradicted by the remainder of the burial assemblage of Sk18. As mentioned, the only other artefacts were pairs of annular brooches and wrist clasps; and within the context of the Scremby cemetery this grave would ordinarily be viewed as comparatively poorly furnished, were it not for the presence of the cup.
Should a single artefact, however unusual, define and potentially elevate the status of an individual when all the other artefacts point to a very ordinary, indeed relatively poor, burial? This is certainly not a call to return to the rather crude employment of ‘wealth scores’ fashionable some decades ago (e.g. Arnold, Reference Arnold, Rahtz, Dickinson and Watts1980); a more subtle approach is needed, starting with the vessel's use in the funerary context. The Scremby Cup was placed at the head end of the grave, and it functioned as a container for food or possibly medicinal products. Only two other containers were excavated from the forty-nine graves at Scremby. Both were plain ceramic vessels without internal deposits and were from well-furnished male graves, which included shield fittings, spears, and knives. The burial of Sk18 is thus different from other female graves, in that the deceased was given a rite otherwise only afforded to males. Next, we must consider the use of an antique vessel. Eckardt & Williams (Reference Eckardt, Williams and Williams2003: 160–61) have observed that Roman material occurs more frequently in the graves of females, and sometimes children, than in those of males; this is perhaps inevitable if one accepts (see discussion of White (Reference White and Southworth1990) and Meaney (Reference Meaney1981) above) that the majority of scavenged material culture either took the form of largely complete female dress accessories, or it performed a more amuletic function, which also seems to have been the preserve of females.
Other levels of meaning might be applicable here. Although focusing on later seventh-century, or ‘conversion period’, cemeteries, some of Sherlock's (Reference Sherlock2016) observations are relevant. While he reaffirms the established narrative that reused artefacts appear to be predominantly found in female graves and indicate elevated status, he states that the intentional reuse of old material culture may have conferred ‘status, faith and antiquity through the female line’ (Sherlock, Reference Sherlock2016: 260). While in an earlier pre-Christian context at Scremby the use of a Roman cup probably had different connotations, a clear message was being conveyed through its use in the funerary rite given to this young female. In this regard it is not unique; indeed, as Eckardt & Williams (Reference Eckardt, Williams and Williams2003: 155) suggest, Roman vessels may have been deliberately sought out to fulfil ceremonial functions in early Anglo-Saxon funerary contexts and this would have perhaps been even more evocative if those who attended the funeral knew that the vessel had come from an earlier grave.
Thus far, the interpretation of the Scremby Cup has centred on the assumption that it was a ‘scavenged’ object and thus totally divorced from its original cultural context. There is, however, another intriguing possibility; that is, that the cup had been carefully curated since its manufacture in the third century. The notion that earlier objects found in Anglo-Saxon contexts might be considered ‘heirlooms’, handed down from generation to generation across the traditional Roman/early medieval divide, has been largely rejected by recent authors (e.g. White, Reference White and Southworth1990: 125–26; Eckardt & Williams, Reference Eckardt, Williams and Williams2003: 155; Costello & Williams, Reference Costello, Williams, Knight, Broughton and Wilkinson2019: 115). The Scremby Cup, being a relatively fragile object, indeed seems unlikely to have remained in active use for several hundred years. As already noted, it bears no signs of damage or repair; however, the same evidence can be used to argue the converse. The cup's extremely fine soldered base remained intact and was firmly in place at the time of its burial in the sixth century, and there is no obvious damage from an earlier episode of deposition. Based on the results of this current analysis, the suggestion that it had not been previously buried is at least as likely as a scenario that supposes it to have been scavenged from a Roman grave. If this was the case, the cup must have been actively curated for several centuries.
If we are to entertain the heirloom hypothesis and the possibility that the individual buried with the cup had a relationship with the object that stretched back into the Roman period, it is important not to conflate this with simplistic notions of a surviving pre-Anglo-Saxon ethnic identity. Indeed, the annular brooches and wrist clasps in the burial of Sk18 belong to traditional forms of Anglian dress; there is nothing uniquely ‘British’ about the burial. Given this, any notion that the Scremby Cup might be an ‘ethnic marker’ of a residual British lineage within an Anglo-Saxon cemetery can be dismissed. It may nevertheless be possible that the Scremby Cup was a possession that had been transferred through a succession of generations, even if its meanings and use had shifted out of all recognition by the time of its final deposition.
Whether a scavenged object or a possession passed through a family, we argue that it is misleading to view the cup purely through a typological lens. Rather than being perceived as ‘Roman’, ‘British’, or indeed ‘Saxon’ by its sixth-century audience, the fact it was clearly of some age is where its real social relevance lay. The placement of the cup, its potential symbolic associations, and its contents represent a ritual not seen in any other female grave in the cemetery. This surely conveyed a powerful message, but one that ultimately is hard to elucidate today. Only through exploring this more nuanced biography, even if this can only be partially understood, can the true significance of the Scremby Cup be fully appreciated.
Acknowledgements
The authors would like to acknowledge the help and advice of Claire Burridge (Universitete i Oslo), Adam Daubney (former Finds Liaison Officer, Lincolnshire County Council), Dave Evans (Wakefield Museum), Pieta Greaves (Drakon Heritage), and Katie Hemer (University College London).
Supplementary Material
To view supplementary material for this article, please visit https://doi.org/10.1017/eaa.2024.12.