Crystalline Structure and Composition of Tin Oxide Film Grown by Reactive Ion Assisted Deposition as a Function of Average Diradiating Energy

Published online by Cambridge University Press:  21 February 2011

W.K. Choi ,
S.K. Song ,
J.S. Cho ,
H.-J. Jung  and
S.K. Koh
W.K. Choi
Affiliation:
Division of Ceramics, Korea Institute of Science and Technology, Cheongryang P.O. Box 131, Seoul, Korea
S.K. Song
Affiliation:
Division of Ceramics, Korea Institute of Science and Technology, Cheongryang P.O. Box 131, Seoul, Korea
J.S. Cho
Affiliation:
Division of Ceramics, Korea Institute of Science and Technology, Cheongryang P.O. Box 131, Seoul, Korea
H.-J. Jung
Affiliation:
Division of Ceramics, Korea Institute of Science and Technology, Cheongryang P.O. Box 131, Seoul, Korea
S.K. Koh
Affiliation:
Division of Ceramics, Korea Institute of Science and Technology, Cheongryang P.O. Box 131, Seoul, Korea
Get access

Abstract

Tin oxide films with highly preferred orientation along <101 axis were grown on Si(100) substrate by using reactive ion assisted deposition method. The impinging average ion energy per depositing Sn atom was changed from 10 to 100 eV/atom. Oxygen content in the deposited tin oxide films increased as average impinging ion energy were raised. The maximum XRD peak intensity appeared when the average energy of about 50 eV/atom was applied. From quantitative Auger electron spectroscopy, characteristic transitional Auger peaks of Sn MNN were shifted to lower kinetic energies as much as 4 ∼ 6±1.0 eV as the Sn4+ component became dominant in the deposited tin oxide films. On the basis of a tin 3d core level spectra analysis by XPS, it was determined that a sizable chemical shift of 1.0±0.02 eV occurred between stannous tin(Sn2+:SnO) and stannic tin(Sn4+:SnO2). The optical transmittance was also measured in the wavelength range from 200 to 800 nm for tin oxide films deposited on BK7 glass substrate.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 396: Symposium A – Ion-Solid Interactions for Materials Modification and Processing , 1995 , 617
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Szcyrbowski, J., Dietrich, A., and Hoffinan, H., Phys. Status. Solidi A, 78, 243 (1983).Google Scholar
2 Grosse, P., Schmitte, F.J., Frank, G., and Kostlin, H., Thin Sild Films, 90, 309 (1982).Google Scholar
3 Bertolotti, M., Ferrari, A., Settle, D., Jaskow, A., Palma, A., and Verona, E., Mater. Lett. 2, 237 (1984).Google Scholar
4 Henrich, V.E. and Cox, P. A., The Surface Science of Metal Oxides(Cambridge University Press, Cambridge, 1994).Google Scholar
5 Nagatomo, T., Endo, M., and Omoto, O., Jpn. J. Appi. Phys. 18, 1103 (1979).Google Scholar
6 Dawar, A.L. and Joshi, J.C., J. Mater. Sci. 19, 1 (1984).Google Scholar
7 Giani, E. and Kelly, R., J. Electrochem. Soc. 121, 394 (1974).Google Scholar
8 Bosnell, J.R. and Waghtone, R., Thin Solid Films, 15, 141 (1973).Google Scholar
9 Park, S.-S. and Mackenzie, J.D., Thin Solid Films, 258, 268 (1995).Google Scholar
10 Ghostagore, R.N., J. Electrochem Soc. 125, 110 (1978).Google Scholar
11 Cuomo, J.J., Rossnagel, S. M., and Kaufman, H. R., Handbook of Ion Beam Processing Technology(Noyes Pub., New Jersey, 1989) p. 194.Google Scholar
12 Sen, S.K., Sen, S., and Bauer, C.L., Thin Solid Films, 82, 157 (1981).Google Scholar
13 Choi, W.K., Cho, J.S., Song, S.K., Jung, H.-J., and Koh, S.K., J. Vac. Sci.Technol. (accepted, Oct. 1995).Google Scholar
14 Robins, J.L., Proc. Phys. Soc. 79, 119 (1962).Google Scholar
15 Lin, A.W.C., Armstrong, N.R., and Kuwana, T., Anal. Chem. 49(8), 1228 (1977).Google Scholar
16 Sen, S.K., Sen, S., and Bauer, C.L., Thin Solid Films, 82, 157 (1981).Google Scholar
17 Lin, A.W.C., Armstrong, N.R., and Kuwana, T., Anal. Chem 49(8), 1228 (1977).Google Scholar
18 Ansell, R. O., Dickinson, T., Povey, A.F., and Sherwood, P.M.A., J. Electrochem. Soc. 124, 1360 (1977).Google Scholar
19 Themlin, J.-M., Chraib, M., Henrard, L., Lambin, P., Darville, J., and Gilles, J.-M., Phys. Rev. B 46, 2460(1992).Google Scholar
20 Courts, T.J., Liand, X., and Cessert, T.A., IEEE Electron. Lett. 26, 660 (1990).Google Scholar
21 Courts, T.J., PearsalL, N.M. and Tarricone, , J. Vac. Sci. Technol. B(2), 140 (1984).Google Scholar
22 Wagner, C.D. and Biloen, P., Surf. Sci. 35, 82 (1973).Google Scholar
23 Lau, C.L. and Wertheim, G.K., J. Vac. Sci. Technol. 15(2), 622 (1978).Google Scholar