Microstructure and Growth Mechanism of Al2O3/Al Ceramic Matrix Composite Made by Directed Oxidation of Al Alloys

Published online by Cambridge University Press:  15 February 2011

C-D. Qin ,
M.O. Lai ,
B. Cotterell  and
S. Shi
C-D. Qin
Affiliation:
Department of Mechanical and Production Engineering 10 Kent Ridge Crescent, Singapore0511
M.O. Lai
Affiliation:
Department of Mechanical and Production Engineering 10 Kent Ridge Crescent, Singapore0511
B. Cotterell
Affiliation:
Department of Mechanical and Production Engineering 10 Kent Ridge Crescent, Singapore0511
S. Shi
Affiliation:
Department of Chemical EngineeringNational University of Singapore, 10 Kent Ridge Crescent, Singapore0511
Get access

Abstract

Since the Lanxide process was advanced for forming of Al2O3 ceramic composite by directed oxidation of Al alloys, much work has been done with various mechanisms being proposed. The mechanisms have claimed that only certain dopants are essential to the growth process. Nevertheless, no united consensus has yet been reached. In the present work, Al alloy containing 5% Mg was oxidised in air for 12 hours at 1150°C with or without surface dopants of MgO or Pd. The resultant composites showed very different microstructures. Without any surface doping, the alloy did not develop any portion of composite as the initial intimate oxide film stops further oxidation. This intimate oxide film can either be broken off by mechanical means or penetrated by reaction with surface dopants, so that the composite can grow and develop. The results show that the previously reported incubation time is not only related to reaction processes but also to the initial mechanical disturbances. Doping with Pd made the composite darker in colour as the grains of the alumina ceramic matrix and inclusions of Al metal are finer. This shows that Pd may make the top oxide layer less intimate, and more nucleation sites are therefore available for oxidation. A new model is presented for oxide sustained growth based on the existence of oxygen active top surface layer and the capillary flow of molten metal around ceramic phase.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 365: Symposium M – Ceramic Matrix Composites–Advanced High-Temperature Structural Materials , 1994 , 133
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Newkirk, M.S., Urquhart, A.W., Zwicker, H.R. & Breval, E., J. Mater. Res. 1, 81 (1986).Google Scholar
2. Salas, O., Ni, H., Jayaram, V., Vlach, K.C., Levi, C.G. & Mehrabian, R., J. Mater. Res. 6, 1964 (1991).Google Scholar
3. Xiao, P. and Derby, B., Proc. British Ceram. Soc. 50, 191 (1993).Google Scholar
4. Xiao, P. and Derby, B., J. Am. Ceram. Soc., 77, 1761 (1994).Google Scholar
5. Breval, E., Aghjanian, K., Biel, J.P. & Antolin, S., J. Am. Ceram. Soc. 76, 1865 (1993).Google Scholar
6. Manor, E., Ni, H., Levi, C.G. & Mehrabian, R., J. Am. Ceram. Soc. 76, 1777 (1993).Google Scholar
7. Backhaus-Ricoult, M. and Dieckmann, R., Ber. Bunsebges. Phys. Chem., 90, 690 (1986).Google Scholar
8. Xiao, P. and Derby, B., J. Am. Ceram. Soc., 77, 1771 (1994).Google Scholar
9. Xiao, P. and Derby, B., J. Euro. Ceram. Soc. 12, 185 (1993).Google Scholar