SiC Thin Films by Chemical Conversion of Single Crystal Si

Published online by Cambridge University Press:  15 February 2011

Chien C. Chiu ,
Chi Kong Kwok  and
Seshu B. Desu
Chien C. Chiu
Affiliation:
Department of Materials Science and EngineeringVirginia Polytechnic Institute and State UniversityBlacksburg, VA 24061
Chi Kong Kwok
Affiliation:
Department of Materials Science and EngineeringVirginia Polytechnic Institute and State UniversityBlacksburg, VA 24061
Seshu B. Desu
Affiliation:
Department of Materials Science and EngineeringVirginia Polytechnic Institute and State UniversityBlacksburg, VA 24061
Get access

Abstract

The reaction of (100)Si with C2H2 in a hot wall CVD reactor has been studied using a X-ray photolectron spectroscopy, and a scanning electron microscopy. The growth of the SiC films was observed through the behavior of Si2p peaks and their plasmons. Smooth surface morphology with a monolayer of SiC was obtained at 950°C for 7 minutes and defects were observed for longer reaction times at this temperature. For higher reaction temperatures (e.g. 1000°C), defects were observed for reaction times as short as 10 seconds. The formation of defects was correlated to the out-diffusion of Si in the carborization process.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 250: Symposium R – Chemical Vapor Deposition of Refractory Metals and Ceramics II , 1991 , 179
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Cheng, T.T., Pirouz, P., and Powell, T.A. in Chemistry and Defects in Semiconductor heterostructures, edited by M. Kawabe, p 229Google Scholar
2. Ikoma, K., Yamanaka, M., Yamaguchi, H., and Schichi, Y., J. Electrochem. Soc. 138, 3208 (1991)CrossRefGoogle Scholar
3. Addamiano, A. and Sprague, J.A., Appl. Phys. Lett. 44, 525 (1984)CrossRefGoogle Scholar
4. Nishino, S., Powell, J.A., and Will, H.A., Appl. Phys. Lett. 42, 460 (1983)CrossRefGoogle Scholar
5. Learn, A.J. and Khan, I.H., Thin Solid Films. 5, 145 (1970)CrossRefGoogle Scholar
6. Mogab, C.J. and Leamy, H.J., J. Appl. Phys. 45, 1075 (1974)CrossRefGoogle Scholar
7. Smith, F.W., Surf. Sci. 80, 388 (1979)CrossRefGoogle Scholar
8. Smith, F. W and Meyerson, B., Thin Solis Films, 60, 227 (1979)CrossRefGoogle Scholar
9. khan, I.H. and Learn, A.J., Appl. Phys. Lett. 15, 410 (1969)CrossRefGoogle Scholar
10. Sugii, T., Aoyama, T, and Ito, T., J. Electrochem. Soc. 137, 989 (1990)CrossRefGoogle Scholar
11. Haq, K.E. and Khan, I.H., J. Vac. Sci. and Tech. 7, 490 (1970)CrossRefGoogle Scholar
12. Kusunoki, I., Hiroi, M., Sato, T., Igari, Y., and Tomoda, S., Appl. Surf. Sci. 45, 171 (1990)CrossRefGoogle Scholar
13. Kim, H.J., Davis, R.F., Cox, X.B., and Linton, R.W., J. Electrochem. Soc. 134, 2269 (1987)CrossRefGoogle Scholar
14. Kim, H.J., Kong, H-S, Edmond, J.A., Glass, J.T., and Davis, R.F.,in Ceramic Transactions Vol 2, Silicon Carbide '87 edited by J.D. Cawley and C.E. Samler.Google Scholar
15. Liaw, P. and Davis, R.F, J. Electrochem. Soc. 132, 642 (1985)CrossRefGoogle Scholar
16. Bozso, F. and Yates, J.T. Jr., J. Appl. Phys. 57, 2771 (1985)CrossRefGoogle Scholar
17. Taylor, P.A., Bozack, M., Choyke, W.J., and Taylor, J.T. Jr., J. Appl. Phys. 65, 1099 (1989)CrossRefGoogle Scholar
18. Iwami, M., Hirai, M., Kusaka, M., Yakota, Y., and Matsunami, H., Jpn. J. Appl. Phys. 28, L293 (1989)CrossRefGoogle Scholar
19. Newman, R.C. and Wakefield, J., in Solid State Physics in Electronics and Telecommunication, edited by M. Desirant and J.L. Michels, p. 318Google Scholar
20. Stinespring, C.D. and Wormhoudt, J.C., J. Appl. Phys. 65, 1733 (1989)CrossRefGoogle Scholar
21. Stinespring, C.D. and Lawson, W.F., Surf. Sci. 150, 209 (1985)CrossRefGoogle Scholar
22. Hong, J.D. and Davis, R.F., J. Am. Ceram. Soc. 63, 546 (1980)CrossRefGoogle Scholar
23. Homg, J.D., Davis, R.F., and Newbury, D.E., J. Mater. Sci. 16, 2485 (1981)CrossRefGoogle Scholar
24. Taubenblatt, M.A. and Helms, C.R., J. Appl. Phys. 59, 1992 (1986)CrossRefGoogle Scholar