Synthesis and Magnetic Properties of Pure and Cobalt-Doped Nanocrystalline Bismuth Ferrite

Published online by Cambridge University Press:  01 February 2011

Gina M Montes ,
Oscar Perales-Perez ,
Boris Rentería  and
Marco Gálvez
Gina M Montes
Affiliation:
gina.montes@upr.edu, University of Puerto Rico at Mayaguez, Mechanical Engineering, Mayaguez, Puerto Rico
Oscar Perales-Perez
Affiliation:
operalesperez@yahoo.com, University of Puerto Rico, Department of Engineering Science and Materials, sTEFANI bUILDING 601, Mayaguez, Mayaguez, 00680, Puerto Rico
Boris Rentería
Affiliation:
brbrenteria@hotmail.com, University of Puerto Rico, Department of Engineering Science and Materials, Mayaguez, Puerto Rico
Marco Gálvez
Affiliation:
marcgalvez2@yahoo.es, University of Puerto Rico at Mayaguez, Physics, Mayaguez, Puerto Rico
Get access

Abstract

Applications of nanocrystalline multiferroics in sensor development, massive memory storage or in the fabrication of new devices taking advantage of the electron charge and spin explains the need of investigating various options to synthesize these types of materials. Among promising candidates, Bismuth ferrite (BiFeO3) is a multiferroic material that exhibits ferromagnetism, ferroelectricity and ferroelasticity. The present research is focused on the systematic study of the polyol synthesis of substrate-less nanocrystalline BiFeO3 particles and its structural and magnetic characterization. As an attempt to explore the possibility of tuning the ferrite magnetic properties, host BiFeO3 was doped with cobalt ions in the 5at. % -10at. % range. Our results suggested that the ferrite formation and its properties were strongly dependent on both, the annealing conditions of the precursors and the concentration of cobalt species. Well-crystallized pure BiFeO3 was produced after annealing the precursor powders for one hour at 800oC. Doping with cobalt ions lowered the temperature at which the nanocrystalline BiFeO3 host structure was developed. The saturation magnetization and coercivity in the nanocrystalline ferrite were strongly influenced by the selected annealing temperatures and dopant concentration. These magnetic parameters varied from 0.30 emu/g and 109.5 Oe up to 4.2 emu/g and 988 Oe for pure and 10 at % Co-doped ferrite, respectively.

Keywords

ferromagneticferroelectricnanostructure
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1256: Symposium N – Functional Oxide Nanostructures and Heterostructures , 2010 , 1256-N06-14
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Zhao, T., Scholl, A. and Zavaliche, F., Nat. Mater., 5, 823–829 (2006).Google Scholar
[2] Liu, H. and, Wang, X., J.Alloys Compd. 485, 769–772 (2009)Google Scholar
[3] Kumar M, M and Palkar V, R, Appl. Phys. Lett. 76 2764 (2000)Google Scholar
[4] Sahu, J.R., Rao, C.N.R., Solid State Sci. 9, 950–954 (2007)Google Scholar
[5] He, Xiaobo and Gao, Lian, Ceram. Int., 35 975–978 (2009)Google Scholar
[6] Park, Tae-Jin, Nano Lett. 7, 766–772 (2007)10.1021/nl063039wGoogle Scholar
[7] Azough, F. et al., J. European Ceramic Soc. 30, 727–736 (2010)Google Scholar
[8] Cedeño-Mattei, Y. and Perales-Perez, O., J. Appl. Phys. 103, 07E512 (2008)Google Scholar
[9] Cedeño-Mattei, Y., and Perales-Perez, O., Microelectron. J. 40, 673–676 (2009)Google Scholar