Carbon Incorporation in Gaas grown by UHVCVD Using Trimethylgallium and Arsine

Published online by Cambridge University Press:  25 February 2011

Seong-Ju Park
Affiliation:
Research Department, Electronics & Telecommunications Research Institute, P.O.Box 8, Daeduk Science Town, Daejeon City, 305–606, Republic of, Korea.
Jeong-Rae Ro
Affiliation:
Research Department, Electronics & Telecommunications Research Institute, P.O.Box 8, Daeduk Science Town, Daejeon City, 305–606, Republic of, Korea.
Jae-Ki Sim
Affiliation:
Research Department, Electronics & Telecommunications Research Institute, P.O.Box 8, Daeduk Science Town, Daejeon City, 305–606, Republic of, Korea.
El-Hang Lee
Affiliation:
Research Department, Electronics & Telecommunications Research Institute, P.O.Box 8, Daeduk Science Town, Daejeon City, 305–606, Republic of, Korea.
Get access

Abstract

We present results of a study on the effect of unprecracked arsine(AsH3) and trimethylgallium(TMGa) on carbon incorporation in UHVCVD(Ultra High Vacuum Chemical Vapor Deposition) grown GaAs epilayers on GaAs(100). Three distinct temperature-dependent regions of growth rates were identified as growth temperature was increased from 570 to 690°C. The growth rates were also strongly dependent on V/III ratio in a range of 5 to 30, which clearly indicates that the growth rate is determined by the amount of arsenic adsorbed on the surface at low V/III ratio and adsorption of TMGa or decomposition process at high V/III ratio. Hall concentration measurements and low temperature photoluminescence data show that the films are all p-type and their impurity concentrations are reduced by two orders of magnitude compared to those of epilayers grown by CBE(Chemical Beam Epitaxy) which employs TMGa and arsenic(precracked arsines) as source materials. Our results indicate that the hydrogen atoms dissociated from adsorbed arsine may remove hydrocarbon species resulting in a significant drop in hole concentration.

Type
Research Article
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Veuhoff, E., Pletschen, W., Balk, P., and Luth, H., J. Cryst. Growth 55, 30 (1981)Google Scholar
[2] Putz, N., Veuhoff, E., Heineke, H., Heyen, M., Luth, H., and Balk, P., J. Vac. Sci. Tech. B3 (2), 671(1985).Google Scholar
[3] Putz, N., Heineke, H., Heyen, M., Balk, P., Weyers, M., Luth, H., J. Cryst. Growth 74, 292(1986).Google Scholar
[4] Calawa, A.R., Appl. Phys. Lett. 38, 701 (1981).Google Scholar
[5] Cunningham, J.E., Trimp, G., Chiu, T.H., Ditzenberger, J.A., Tsang, W.T., Sergent, A.M. and Lang, D.V., J. Cryst. Growth 95, 185 (1989).Google Scholar
[6] Calawa, A.R., Appl. Phys. Lett. 33, 1020 (1978).Google Scholar
[7] Hafich, M.J., Lee, H.Y., Silvestre, P. and Robinson, G.Y., J. Cryst. Growth 111, 507(1991).Google Scholar
[8] Chandra, A., Wood, C. E. C., Woodard, D. W., and Eastman, L., Solid-State Elec. 22, 645(1979).Google Scholar
[9] Abernathy, C. R., Pearton, S. J., Ren, F., Hobson, W. S., Fullowan, T. R., Katz, A., Jordan, A. S., and Kovalchik, J., J. Cryst. Growth 105, 375 (1990).Google Scholar
[10] Konagai, M., Yamada, T., Akatsuka, T., Nozaki, S., Miyake, R., Saito, K., Fukamachi, T., Tokumitsu, E. and Takahashi, K., J. Cryst. Growth 105, 359 (1990).Google Scholar