In-Situ Aluminum-Induced Crystallization of Si Thin-Films on Glass Substrates above the Eutectic Temperature using HW-CVD

Published online by Cambridge University Press:  21 March 2011

Ozgenc Ebil ,
Roger Aparicio  and
Robert Birkmire
Ozgenc Ebil
Affiliation:
Institute of Energy Conversion, University of Delaware Newark, DE 19716 U.S.A.
Roger Aparicio
Affiliation:
Institute of Energy Conversion, University of Delaware Newark, DE 19716 U.S.A.
Robert Birkmire
Affiliation:
Institute of Energy Conversion, University of Delaware Newark, DE 19716 U.S.A.
Get access

Abstract

The growth of poly-Si films on glass substrates using an in-situ aluminum-induced crystallization (AIC) process above the Si-Al eutectic temperature of 577°C is discussed. Silicon films were deposited by Hot-Wire Chemical Vapor Deposition (HW-CVD) onto Al coated Corning 7059 glass substrates. The back surface coverage and the average grain size of the films were compared as a function of growth rate and the Si/Al thickness ratio. SEM and EDS analysis of samples with a Si/Al ratio of 1 revealed two domains in the films which varied in morphology and composition; rougher areas containing a mixture of Si and Al with Al content up to 35%, and relatively smoother areas composed of almost entirely Si. This non-uniform morphology seems to be the result of the absence of a native oxide layer when a liquid phase is formed during the deposition. Si grains as large as 50 m m in diameter and back surface coverage up to 90% were obtained for both the Si/Al ratios of 1 and 5. However, no continuous Si films were obtained. The sample with a Si/Al ratio of 1 had columnar grains reaching to the film surface, whereas on the Si/Al ratio of 5 large Si grains did not extend to the film surface.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 808: Symposium A – Amorphous and Nanocrystaline Silicon Science and Technology-2004 , 2004 , A4.24
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Yoon, S. Y., Kim, K. H., Kim, C. O., Oh, J. Y. and Jang, J., J. Appl. Phys. 82, 5865 (1997).Google Scholar
2. Ebil, O., Aparicio, R., Hazra, S., Birkmire, R. W., and Sutter, E., J. Thin Solid Films 430, 120 (2003).Google Scholar
3. Heya, A., Masuda, A., and Matsumura, H., Appl. Phys. Lett. 74, 2143 (1999).Google Scholar
4. Heya, A., Izumi, A., Masuda, A., and Matsumura, H., Jpn. J. Appl. Phys. 39, 3888 (2000).Google Scholar
5. Maa, J.-S. and Lin, S.-J., Thin-Solid-Films 64, 63 (1979).Google Scholar
6. Masaki, Y., Ogata, T., Ogawa, H., and Jones, D. I., J. Appl. Phys. 76, 5225 (1994).Google Scholar
7. Widenborg, P. I. and Aberle, A. G., J. Crystal Growth 242, 270 (2002).Google Scholar
8. Nast, O. and Hartmann, A. J., J. Appl. Phys. 88, 716 (2000).Google Scholar
9. Nast, O. and Wenham, S. R., J. Appl. Phys. 88, 124 (2000).Google Scholar
10. Niira, K., Hakuma, H., Komoda, M., Fukui, K., and Shirasawa, K., Solar Energy Materials & Solar Cells 69, 107 (2001).Google Scholar
11. Haque, M. S., Naseem, H. A., and Brown, W. D., J. Appl. Phys. 75, 3928 (1994).Google Scholar
12. Nast, O., PhD. Thesis, University of Marburg, 2000.Google Scholar
13. Tu, K. N., Appl. Phys. Lett. 27, 221 (1975).Google Scholar
14. Hiraki, A., J. Electrochem. Soc. 127, 2662 (1980).Google Scholar
15. Ebil, O., PhD. Thesis, University of Delaware, 2004.Google Scholar